Method of manufacturing glass plate having curved surface shape, and glass plate having a curved surface shape

Patent metadata

Field	Value
Publication number	US-10087100-B2
Application number	US-201414769130-A
Country	US
Kind code	B2
Filing date	Feb 13, 2014
Priority date	Apr 10, 2013
Publication date	Oct 2, 2018
Grant date	Oct 2, 2018

Abstract

Provided is a method that can manufacture a glass plate having a curved surface shape with high surface accuracy even without polishing the surface after forming and a glass plate manufactured by the method. The method of manufacturing a glass plate having a curved surface shape includes the steps of: preparing an original glass plate, a forming die ( 10 ) including a recess ( 11 ) corresponding to the curved surface shape, and a forming tool ( 20 ) operable to press the original glass plate ( 2 ); placing the original glass plate ( 2 ) on the recess ( 11 ) in the forming die ( 10 ); heating the original glass plate ( 2 ) and the forming die ( 10 ); maintaining a temperature of a surface of the recess ( 11 ) in the forming die at a temperature lower than a temperature of the original glass plate ( 2 ); and giving the original glass plate ( 2 ) the curved surface shape by pressing the heated original glass plate ( 2 ) with the forming tool ( 20 ) to deform the original glass plate ( 2 ) while bringing the original glass plate ( 2 ) into contact with the surface of the recess ( 11 ).

First claim

The invention claimed is:

1. A method of manufacturing a glass plate having a curved surface shape, the method comprising the steps of:
preparing an original glass plate, a forming die including a recess corresponding to the curved surface shape, and a forming tool operable to press the original glass plate;
placing the original glass plate on the recess in the forming die;
heating the original glass plate and the forming die;
maintaining a temperature of a surface of the recess in the forming die at a temperature lower than a temperature of the original glass plate; and
giving the original glass plate the curved surface shape by pressing the heated original glass plate with the forming tool to deform the original glass plate while bringing the original glass plate into contact with the surface of the recess; wherein
the forming tool includes a raised portion having a radius of curvature smaller than that of the curved surface shape and a central portion of the original glass plate is deformed by pressing only the central portion with the raised portion, and portions of the original glass plate outside the central portion thereof are then deformed by inclining and turning the forming tool from side to side and thus pressing the original glass plate with a curved surface of the raised portion.

2. The method of manufacturing a glass plate having a curved surface shape according to claim 1 , wherein a temperature at which the original glass plate is heated is not lower than a glass transition point of glass forming the original glass plate and not higher than a softening point of the glass.

3. The method of manufacturing a glass plate having a curved surface shape according to claim 1 , wherein the temperature of the surface of the recess is maintained at a temperature not lower than a strain point of glass forming the original glass plate and not higher than a glass transition point of the glass.

4. The method of manufacturing a glass plate having a curved surface shape according to claim 1 , wherein a coolant operable to cool the forming die is introduced into the forming die.

5. The method of manufacturing a glass plate having a curved surface shape according to claim 1 , wherein the original glass plate is deformed by pressing the original glass plate with the forming tool while introducing a coolant into the forming tool.

6. A method of manufacturing a glass plate having a curved surface shape, the method comprising the steps of:
preparing an original glass plate, a forming die including a recess corresponding to the curved surface shape, and a forming tool operable to press the original glass plate;
placing the original glass plate on the recess in the forming die;
heating the original glass plate and the forming die;
maintaining a temperature of a surface of the recess in the forming die at a temperature lower than a temperature of the original glass plate; and
giving the original glass plate the curved surface shape by pressing the heated original glass plate with the forming tool to deform the original glass plate while bringing the original glass plate into contact with the surface of the recess; wherein
the forming tool is a bar-shaped forming tool and the original glass plate is given the curved surface shape by pressing the original glass plate with the forming tool while shifting a position of the forming tool relative to the original glass plate; and
the original glass plate is deformed by pressing the original glass plate more than once at the same position with the forming tool.

Assignees

• Nippon Electric Glass Co

Inventors

• Ikemoto Masayuki
• Odani Osamu
• Wada Masanori

Classifications

• C03B23/0307

  Press-bending involving applying local or additional heating, cooling or insulating means · CPC title

• C03B23/0013 Primary

  by pressing (C03B21/04, C03B23/02, C03B23/04, C03B23/18, C03B23/26 take precedence) · CPC title

• Y10T428/24628

  Nonplanar uniform thickness material · CPC title

• C03B23/0302 Primary

  between opposing full-face shaping moulds · CPC title