Cutting tool made of diamond-coated cemented carbide and method for producing the same

Patent metadata

Field	Value
Publication number	US-10086438-B2
Application number	US-201415038942-A
Country	US
Kind code	B2
Filing date	Nov 28, 2014
Priority date	Nov 29, 2013
Publication date	Oct 2, 2018
Grant date	Oct 2, 2018

Abstract

A cutting tool made of diamond-coated cemented carbide includes: a tool body made of tungsten carbide-based cemented carbide including: 3 to 15 mass % of Co; at least one of TaC and NbC of which a total amount is 0.1 to 3.0 mass %; and a balance including WC; and a diamond film coating the tool body, the tool body has a plurality of protrusions on a surface of the tool body, an upper portion of each of the protrusions is made of the at least one of TaC and NbC, and a lower portion of each of the protrusions is made of WC and Co, the lower portion being under the upper portion.

First claim

The invention claimed is:

1. A cutting tool made of diamond-coated cemented carbide, the cutting tool comprising:
a tool body made of tungsten carbide-based cemented carbide including:
3 to 15 mass % of Co;
at least one of TaC and NbC of which a total amount is 0.1 to 3.0 mass %; and
a balance including WC; and

a diamond film coating the tool body,
wherein the tool body has a plurality of protrusions on a surface of the tool body, of which an average height is 1.0 to 3.0 μm, an average width is 0.5 to 6.0 μm, and an average aspect ratio of the height to the width is 0.5 to 3.0;
an upper portion of each of the protrusions is made of the at least one of TaC and NbC;
a lower portion of each of the protrusions is made of WC and Co, the lower portion being under the upper portion; and
a portion of Co is removed in a region of the tool body between the surface of the tool body and a depth of 6 μm from the surface.

2. The cutting tool made of diamond-coated cemented carbide according to claim 1 , wherein the number of the protrusions per unit area is 500 to 10000/mm 2 .

3. The cutting tool made of diamond-coated cemented carbide according to claim 1 , wherein an average film thickness of the diamond film is 3 to 30 μm.

4. The cutting tool made of diamond-coated cemented carbide according to claim 1 , wherein
the diamond film has a plurality of bumps on a surface of the diamond film, of which an average height is 1.0 to 3.0 μm, and an average width is 3.0 to 20.0 μm.

5. The cutting tool made of diamond-coated cemented carbide according to claim 4 , wherein the number of the bumps per unit area is 500 to 10000/mm 2 .

6. The cutting tool made of diamond-coated cemented carbide according to claim 1 , wherein a Co content is 2 to 13 mass % in the lower portion.

7. The cutting tool made of diamond-coated cemented carbide according to claim 1 , wherein a total amount of the at least one of TaC and NbC is 95 to 100 mass % in the upper portion.

8. A method for producing the cutting tool made of diamond-coated cemented carbide according to claim 1 , the method comprising:
a granulating step of granulating a Co powder, at least one of a TaC powder and a NbC powder, and a WC powder using a spray dryer at 190 to 210° C.;
a sintering step of: mixing the granulated Co powder, the at least one of TaC powder and NbC powder, and the WC powder with each other to obtain a mixture and then holding the mixture at 0.1 to 10 Pa and 1380 to 1500° C. for 1 to 2 hours to sinter the mixture and form the tool body;
a first pretreatment step of immersing the tool body in an acid solution containing 0.4 to 1.0 volume % of dilute sulfuric acid and 2 to 5 volume % of hydrogen peroxide water at room temperature for 15 to 25 seconds;
a second pretreatment step of subjecting the tool body which has been subjected to the first pretreatment step to electrolytic etching by immersing the tool body in an alkaline etchant with a concentration of 5 to 15 volume % containing sodium hydroxide for 30 to 60 minutes while an electric current at 1.5 to 2.5 A/dm 2 is passed through the alkaline etchant;
a third pretreatment step of immersing the tool body which has been subjected to the second pretreatment step in an acid solution containing 0.4 to 1.0 volume % of dilute sulfuric acid and 2 to 5 volume % of hydrogen peroxide water at room temperature for 8 to 15 seconds; and
a step of coating the tool body which has been subjected to the third pretreatment step with the diamond film.

9. The cutting tool made of diamond-coated cemented carbide according to claim 1 , a portion of the surface of the tool body where protrusions are not formed is substantially flat.

Assignees

• Mitsubishi Materials Corp

Inventors

• Takashima Hideaki
• Takaoka Hidemitsu

Classifications

• B22F2301/15

  Nickel or cobalt · CPC title

• B22F3/10

  Sintering only · CPC title

• C04B2237/405

  Iron metal group, e.g. Co or Ni · CPC title

• B22F2998/10

  Processes characterised by the sequence of their steps · CPC title

• B23B2226/275

  Carbon fibre reinforced carbon composites · CPC title