Continuous process for producing electrodes for supercapacitors having high energy densities

Patent metadata

Field	Value
Publication number	US-10083801-B2
Application number	US-201815888461-A
Country	US
Kind code	B2
Filing date	Feb 5, 2018
Priority date	Oct 13, 2015
Publication date	Sep 25, 2018
Grant date	Sep 25, 2018

Abstract

A process for producing a supercapacitor cell, comprising: (a) Continuously feeding a conductive porous layer to a cathode material impregnation zone, wherein the conductive porous layer contains interconnected electron-conducting pathways and at least 70% by volume of pores; (b) Impregnating a wet cathode active material mixture (containing a cathode active material and an optional conductive additive mixed with a liquid electrolyte) into pores of this porous layer to form a cathode electrode; (c) Preparing an anode electrode in a similar manner; and (d) Stacking an anode electrode, a porous separator, and a cathode electrode to form the supercapacitor, wherein the anode electrode and/or the cathode electrode has a thickness no less than 100 μm; and/or wherein the anode or cathode active material constitutes an electrode active material loading no less than 7 mg/cm 2 in the anode or the cathode.

First claim

We claim:

1. A supercapacitor cell comprising an anode, containing an anode active material, a cathode containing a cathode active material, a porous separator disposed between said anode and said cathode, and an electrolyte in ionic contact with said anode active material and said cathode active material, wherein at least one of said anode and cathode comprise a foam current collector having interconnected electron-conducting pathways, said current collector having 70% to 99% by volume of pores, and wherein said pores contain said electrolyte and said anode active material or cathode active material residing therein.

2. The supercapacitor of claim 1 wherein said foam current collector is selected from the group consisting of metal foam, metal web, metal screen, perforated metal sheet-based three dimensional structure, metal fiber mat, metal nanowire mat, conductive polymer nanofiber mat, conductive polymer foam, conductive polymer-coated fiber foam, carbon foam, graphite foam, carbon aerogel, carbon xerogel, graphene foam, graphene oxide foam, reduced graphene oxide foam, carbon fiber foam, graphite fiber foam, exfoliated graphite foam, and combinations thereof.

3. The supercapacitor of claim 1 wherein said foam current collector has a thickness from 100 μm to 5 mm.

4. The supercapacitor of claim 1 wherein said foam current collector comprises pores substantially having a size from 10 nm to 50 μm.

5. The supercapacitor of claim 1 wherein said anode or cathode comprises electrode active material with a loading level from 7 mg/cm 2 to 30 mg/cm 2 .

6. The supercapacitor of claim 1 , wherein said substantially all of said anode active material or said cathode active material is less than 25 μm from a pore wall.

7. The supercapacitor of claim 1 , having a gravimetric energy density from 9.6 Wh/kg to 97.7 Wh/kg.

8. The supercapacitor of claim 1 , having a volumetric energy density from 3 Wh/L to 12.3 Wh/L.

9. The supercapacitor of claim 1 , wherein said anode or said cathode contains graphene sheets as the only electrode active material and does not contain any other electrode active material.

10. The supercapacitor of claim 1 , wherein said anode or said cathode contains the following materials as the only electrode active material in said anode or cathode: (a) graphene sheets alone; (b) graphene sheets mixed with a carbon material; (c) graphene sheets mixed with a partner material that forms a redox pair with said graphene sheets to develop pseudo-capacitance; or (d) graphene sheets and a carbon material mixed with a partner material that forms a redox pair with said graphene sheets or said carbon material to develop pseudo-capacitance, and wherein there is no other electrode active material in said anode or cathode.

11. The supercapacitor of claim 1 wherein said anode active material or cathode active material residing in the pores contains single-layer graphene and few-layer graphene having from 1 to 10 graphene planes; and said anode active material or cathode active material has a specific surface area from 500 m 2 /g to 2,675 m 2 /g when measured in a dried state.

12. The supercapacitor of claim 1 wherein said anode active material or cathode active material residing in the pores contains a graphene material selected from the group consisting of pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, graphene bromide, graphene iodide, hydrogenated graphene, nitrogenated graphene, boron-doped graphene, nitrogen-doped graphene, chemically functionalized graphene, physically or chemically activated or etched versions thereof, conductive polymer coated or grafted versions thereof, and combinations thereof.

13. The supercapacitor of claim 12 wherein said chemically functionalized graphene contains surface functional groups selected from quinone, hydroquinone, quaternized aromatic amines, mercaptans, or disulfides.

14. The supercapacitor of claim 1 , wherein said anode active material or cathode active material residing in the pores contains a material selected from graphene materials, activated carbon, activated mesocarbon micro beads, activated graphite, activated or chemically etched carbon black, activated hard carbon, activated soft carbon, carbon nanotube, carbon nanofiber, activated carbon fiber, activated graphite fiber, exfoliated graphite worms, activated graphite worms, activated expanded graphite flakes, or a combination thereof, and said pores further comprise a redox pair partner material selected from a metal oxide, a conducting polymer, an organic material, a non-graphene carbon material, an inorganic material, or a combination thereof.

15. The supercapacitor of claim 14 , wherein said metal oxide is selected from RuO 2 , IrO 2 , NiO, MnO 2 , VO 2 , V 2 O 5 , V 3 O 8 , TiO 2 , Cr 2 O 3 , Co 2 O 3 , Co 3 O 4 , PbO 2 , Ag 2 O, or a combination thereof.

16. The supercapacitor of claim 14 wherein said conductive polymer is selected from the group consisting of polyacetylene, polypyrrole, polyaniline, polythiophene, derivatives thereof, and combinations thereof.

17. The supercapacitor of claim 14 , wherein said inorganic material is selected from a metal carbide, metal nitride, metal boride, metal dichalcogenide, or a combination thereof.

18. The supercapacitor of claim 14 , wherein said metal oxide or said inorganic material is selected from an oxide, dichalcogenide, trichalcogenide, sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, vanadium, chromium, cobalt, manganese, iron, or nickel in a nanowire, nanodisc, nanoribbon, or nanoplatelet form.

19. The supercapacitor of claim 14 , wherein said inorganic material is selected from nanodiscs, nanoplatelets, nano-coating, or nanosheets of an inorganic material selected from: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of a transition metal; (d) boron nitride, or (e) a combination thereof; wherein said nanodiscs, nanoplatelets, or nanosheets have a thickness less than 100 nm.

20. The supercapacitor of claim 14 , wherein said anode active material or said cathode active material contains nanodiscs, nanoplatelets, nano-coating, or nanosheets of an inorganic material selected from: (i) bismuth selenide or bismuth telluride, (ii) transition metal dichalcogenide or trichalcogenide, (iii) sulfide, selenide, or telluride of a transition metal; (iv) boron nitride, or (v) a combination thereof, wherein said nanodiscs, nanoplatelets, nano-coating, or nanosheets have a thickness less than 100 nm.

21. The supercapacitor of claim 1 , wherein said anode active material is different from said cathode active material.

22. The supercapacitor of claim 1 , which is a lithium-ion capacitor or sodium-ion capacitor.

23. The supercapacitor of claim 22 , wherein said lithium-ion capacitor contains an anode active material selected from the group consisting of:
a. prelithiated particles of natural graphite, artificial graphite, mesocarbon microbeads (MCMB), and carbon;
b. prelithiated particles or coating of silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), nickel (Ni), cobalt (Co), manganese (Mn), titanium (Ti), iron (Fe), and cadmium (Cd);
c. prelithiated alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, or Cd with other elements, wherein said alloys or compounds are stoichiometr

Assignees

• Nanotek Instruments Inc

Inventors

• Zhamu Aruna
• Jang Bor Z

Classifications

• H01G11/38

  Carbon pastes or blends; Binders or additives therein · CPC title

• H01G11/86 Primary

  specially adapted for electrodes (carbonisation or activation of carbon for the manufacture of electrodes H01G11/34) · CPC title

• H01G11/84

  Processes for the manufacture of hybrid or EDL capacitors, or components thereof · CPC title

• H01G11/36

  Nanostructures, e.g. nanofibres, nanotubes or fullerenes · CPC title

• H01G11/26

  characterised by their structure, e.g. multi-layered, porosity or surface features · CPC title