Cubic boron nitride sintered body and coated cubic boron nitride sintered body

Patent metadata

Field	Value
Publication number	US-10081577-B2
Application number	US-201515538604-A
Country	US
Kind code	B2
Filing date	Dec 24, 2015
Priority date	Dec 24, 2014
Publication date	Sep 25, 2018
Grant date	Sep 25, 2018

Abstract

A cBN sintered body has 40%-85% cBN by volume and 15% to 60% binder phase by volume. and inevitable impurities. The binder phase has an Al compound including Al and at least one element selected from N, O and B, and a Zr compound including Zr and at least one element selected from C, N, O and B. The Zr compound includes ZrO, or ZrO and ZrO 2 . In an X-ray diffraction, where a peak intensity of a (111) plane of the ZrO is I 1 , a peak intensity of a (101) plane of tetragonal ZrO 2 is I 2t and a peak intensity of a (111) plane of cubic ZrO 2 is I 2c , a ratio of the intensity of I 1 to total intensities of I 1 , I 2t and I 2c is 0.6-1.0, and an average grain size of the Al compound is 80 nm-300 nm.

First claim

The invention claimed is:

1. A cubic boron nitride sintered body comprising:
a cubic boron nitride with 40% by volume or more and 85% by volume or less; a binder phase with 15% by volume or more and 60% by volume or less; and inevitable impurities, wherein
the binder phase comprises:
an Al compound comprising an Al element and at least one element selected from the group consisting of N, O and B; and
a Zr compound comprising a Zr element and an O element and at least one element selected from the group consisting of C, N and B,
the Zr compound comprises ZrO, or ZrO and ZrO 2 ,
when a peak intensity of a (111) plane of the ZrO is represented as I 1 , a peak intensity of a (101) plane of tetragonal ZrO 2 is represented as I 2t , and a peak intensity of a (111) plane of cubic ZrO 2 is represented as I 2c in an X-ray diffraction, a ratio [I 1 /(I 1 +I 2t +I 2c )] of the intensity of I 1 based on a sum of the intensities of I 1 , I 2t and I 2c is 0.6 or more and 1.0 or less, and
an average grain size of the Al compound is 80 nm or more and 300 nm or less.

2. The cubic boron nitride sintered body according to claim 1 , wherein
the Al compound comprises Al 2 O 3 ,
a crystal structure of the Al 2 O 3 is α-Al 2 O 3 , and
when a peak intensity of a (110) plane of the α-Al 2 O 3 is represented as I 3 in an X-ray diffraction, a ratio [I 1 /I 3 ] of the intensity of I′ based on the intensity of I 3 is 0.3 or more and 0.8 or less.

3. The cubic boron nitride sintered body according to claim 1 , wherein the Zr compound is 1% by volume or more and 10% by volume or less based on the whole cubic boron nitride sintered body.

4. The cubic boron nitride sintered body according to claim 1 , wherein an average particle size of the cubic boron nitride is 0.2 μm or more and 2.0 μm or less.

5. A coated cubic boron nitride sintered body comprising a film formed onto a surface of the cubic boron nitride sintered body according to claim 1 .

6. The coated cubic boron nitride sintered body according to claim 5 , wherein the film comprises at least one or more elements selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Al and Si, and at least one or more elements selected from the group consisting of C, N, O and B.

7. The coated cubic boron nitride sintered body according to claim 5 , wherein the film is a single layer film or a laminated film of two or more layers.

8. The coated cubic boron nitride sintered body according to claim 5 , wherein a total film thickness of a whole film is 0.5 μm or more and 20 μm or less in terms of an average film thickness.

9. The coated cubic boron nitride sintered body according to claim 6 , wherein a total film thickness of a whole film is 0.5 μm or more and 20 μm or less in terms of an average film thickness.

10. The coated cubic boron nitride sintered body according to claim 9 , wherein the film is a single layer film.

11. The coated cubic boron nitride sintered body according to claim 9 , wherein the film is a laminated film of two or more layers.

12. The cubic boron nitride sintered body according to claim 2 , wherein the Zr compound is 1% by volume or more and 10% by volume or less based on the whole cubic boron nitride sintered body.

13. The cubic boron nitride sintered body according to claim 12 , wherein an average particle size of the cubic boron nitride is 0.2 μm or more and 2.0 μm or less.

Assignees

• Tungaloy Corp

Inventors

• Hirano Yusuke
• Shiro Kentaro

Classifications

• C04B2235/3839

  Refractory metal carbides · CPC title

• C04B2235/785

  Submicron sized grains, i.e. from 0,1 to 1 micron · CPC title

• C04B2235/3225

  Yttrium oxide or oxide-forming salts thereof · CPC title

• C04B2235/786

  Micrometer sized grains, i.e. from 1 to 100 micron · CPC title

• C04B2235/3246

  Stabilised zirconias, e.g. YSZ or cerium stabilised zirconia · CPC title