Thermally conductive complex oxide, production method therefor, thermally conductive complex oxide-containing composition, and use therefor

Patent metadata

Field	Value
Publication number	US-10072195-B2
Application number	US-201515122321-A
Country	US
Kind code	B2
Filing date	Mar 12, 2015
Priority date	Mar 14, 2014
Publication date	Sep 11, 2018
Grant date	Sep 11, 2018

Abstract

The thermally conductive composite oxide of the present invention has excellent physical properties, such as high thermal conductivity, water resistance, acid resistance, electric resistance, and electric insulation, required for coating films, films, and articles thereof. Paints or resins including the composite oxide can provide coating films, films, and articles having such properties without treating of a surface, etc. The composite oxide has a spinel structure and contains aluminum as a main metal component and at least one metal other than aluminum, which is magnesium, zinc, calcium, and/or strontium, and has a ratio (b mol)/(a mol) in a range of 0.1 or more and 1.0 or less, where the ratio (b mol)/(a mol) is a number of moles (b) of the metal other than aluminum to that of moles (a) of an aluminum element derived from an alumina-based compound. The thermally conductive composite oxide has Mohs hardness of less than 9.

First claim

The invention claimed is:

1. A thermally conductive composite oxide comprising:
aluminum as a main metal component; and
at least one metal other than aluminum,
wherein the thermally conductive composite oxide is a fired product of a precursor comprising: at least (i) an alumina-based compound comprising the aluminum; and (ii) a compound comprising the at least one metal other than aluminum,
the at least one metal other than aluminum is at least one metal selected from the group consisting of magnesium, zinc, calcium, and strontium,
a ratio (b mol)/(a mol) of a number of moles (b) of the at least one metal other than aluminum relative to a number of moles (a) of the aluminum as an aluminum element in the alumina-based compound is in a range of 0.1 or more and 1.0 or less,
the thermally conductive composite oxide is a composite oxide having a flake shape or a needle shape and having a spinel structure,
the thermally conductive composite oxide has an average major axis diameter in a range from 5 to 40 μm and an average minor axis diameter in a range from 0.1 to 30 μm, and
a Mohs hardness of the thermally conductive composite oxide is less than 9.

2. The thermally conductive composite oxide according to claim 1 ,
wherein a content ratio of each metal relative to a total amount of the aluminum and the at least one metal other than aluminum in the thermally conductive composite oxide is in a range from 50 to 90 mol % for the aluminum derived from the alumina-based compound and is in a range from 10 to 50 mol % for the at least one metal other than aluminum.

3. The thermally conductive composite oxide according to claim 1 ,
wherein the alumina-based compound is alumina, aluminum hydroxide, or an alumina hydrate.

4. The thermally conductive composite oxide according to claim 1 ,
wherein the compound of the at least one metal other than aluminum is at least one compound selected from the group consisting of an oxide, a hydroxide, a sulfate, a nitrate, a chloride, a carbonate, a basic carbonate, an oxalate, and an acetate of the at least one metal other than aluminum.

5. A process for producing the thermally conductive composite oxide according to claim 1 , the process comprising:
adding an alkali agent and an aqueous solution of the compound of the at least one metal other than aluminum to an aqueous suspension solution of the alumina-based compound so as to deposit a precipitate on a surface of the alumina-based compound, thereby producing a precursor;
firing the produced precursor; and
thereafter pulverizing the fired product,
wherein the alumina-based compound has a flake shape or a needle shape.

6. A thermally conductive composite oxide-containing composition, comprising:
the thermally conductive composite oxide according to claim 1 ; and
a thermally conductive filler.

7. An article comprising a coating liquid composition or a resin composition,
wherein the coating liquid composition and the resin composition comprise the thermally conductive composite oxide according to claim 1 , and optionally further comprise a thermally conductive filler.

8. A process for producing a thermally conductive composite oxide, the process comprising:
adding an alkali agent and an aqueous solution of a compound of a metal other than aluminum to an aqueous suspension solution of an alumina-based compound so as to deposit a precipitate on a surface of the alumina-based compound, thereby producing a precursor;
firing the produced precursor at a temperature in a range from 1000° C. to 1500° C.; and
thereafter pulverizing the fired product,
wherein the thermally conductive composite oxide comprises:
aluminum as a main metal component; and
the metal other than aluminum,

wherein the metal other than aluminum is at least one metal selected from the group consisting of magnesium, zinc, calcium, and strontium, and
a ratio (b mol)/(a mol) of a number of moles (b) of the at least one metal other than aluminum relative to a number of moles (a) of the aluminum as an aluminum element in the alumina-based compound is in a range of 0.1 or more and 1.0 or less.

9. The process for producing a thermally conductive composite oxide according to claim 8 , wherein the precipitate deposited on the surface of the alumina-based compound is at least one material selected from the group consisting of an oxide, a hydroxide, and a carbonate, of the at least one metal other than aluminum.

Assignees

• Dainichiseika Color Chem

Inventors

• Nishio Akira
• Kawakami Toru
• Yamane Kenichi
• YAMAMURA Naotsugu
• Tominaga Shingo

Classifications

• C09C1/40

  Compounds of aluminium {(C09C1/0009, C09C1/0015, C09C1/0078, C09C1/32 take precedence)} · CPC title

• C01G9/00

  Compounds of zinc · CPC title

• C01P2004/54

  Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension · CPC title

• C09D1/00

  Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances · CPC title

• C01P2004/62

  Submicrometer sized, i.e. from 0.1-1 micrometer · CPC title