Austenitic stainless steel sheet and metal gasket

Patent metadata

Field	Value
Publication number	US-10060003-B2
Application number	US-201515503434-A
Country	US
Kind code	B2
Filing date	Aug 10, 2015
Priority date	Aug 19, 2014
Publication date	Aug 28, 2018
Grant date	Aug 28, 2018

Abstract

A hot rolled austenitic stainless steel sheet contains 0.030 to 0.300% of C, from 0.30 to 3.20% of Si, from 0.90 to 17.00% of Mn, from 1.00 to 8.00% of Ni, from 14.00 to 19.00% of Cr, from 0.50 to 3.50% of Cu, from 0.045 to 0.250% of N, from 0.0001 to 0.0300% of Al, from 0 to 0.50% of V, from 0 to 0.50% of Nb, from 0 to 0.30% of Ti, and from 0 to 0.010% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, has a converted average composition of an oxide based inclusion that contains 30% by mass or less of Al 2 O 3 , 60% by mass or less of SiO 2 , and 15% by mass or more of MnO, and satisfies MnO 3 —3SiO 2 +110. Anisotropy of workability and fatigue resistance characteristics caused by an oxide based inclusion is decreased.

First claim

The invention claimed is:

1. A cold rolled austenitic stainless steel sheet derived from a hot rolled austenitic stainless steel having a steel composition that contains from 0.030 to 0.300% of C, from 0.30 to 3.20% of Si, from 0.90 to 17.00% of Mn, from 1.00 to 8.00% of Ni, from 14.00 to 19.00% of Cr, from 0.50 to 3.50% of Cu, from 0.045 to 0.250% of N, from 0.0001 to 0.0300% of Al, from 0 to 0.50% of V, from 0 to 0.50% of Nb, from 0 to 0.30% of Ti, and from 0 to 0.010% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, and has an Md 30 value defined by the following expression (1) of 50.0 or less and a δ 1230 value defined by the following expression (2) of 8.0 or less, and having an average composition of an oxide based inclusion observed in a metal structure that contains 30% by mass or less of Al 2 O 3 , 60% by mass or less of SiO 2 , and 15% by mass or more of MnO, in terms of converted mass ratio of Al 2 O 3 , SiO 2 , and MnO, and satisfies the following expression (3), wherein a heating temperature at which the Vickers hardness of a plate surface of the cold rolled austenitic stainless steel after being subjected to a heat treatment of 120 hours falls to ⅔ of the Vickers hardness on a rolled surface of the sheet, Ho (HV), is at least 800° C.:
Md 30 =551−462(C+N)−9.2Si−8.1Mn−29(Ni+Cu)−13.7Cr  (1)

δ 1230 =−101.5−78.6C+3.1Si+0.4Mn−2.4M+7.7Cr−1.5Cu−51.4N  (2)

MnO≥−3SiO 2 +110  (3)

wherein in the expressions (1) and (2), the element symbols represent the percentages by mass of the elements respectively in the steel composition, and in the expression (3), MnO and SiO 2 represent the converted percentages by mass of MnO and SiO 2 respectively in the average composition of the oxide based inclusion.

2. The cold rolled austenitic stainless steel sheet according to claim 1 , which has a Vickers hardness on the surface of the rolled sheet of from 400 to 460 HV.

3. The cold rolled austenitic stainless steel sheet according to claim 1 , which has a thickness of from 0.05 to 0.5 mm.

4. The cold rolled austenitic stainless steel sheet according to claim 1 , which has a Vickers hardness on the rolled surface of the sheet of from 400 to 460 HV, and a thickness of from 0.05 to 0.5 mm.

5. A metal gasket comprising the cold rolled steel sheet according to claim 1 having been formed, having a bead formed by press forming, and being used by pressing an apex of the bead onto a contact material.

6. A metal gasket comprising the cold rolled steel sheet according to claim 1 having been formed and then subjected to an aging treatment at from 100 to 500° C., having a bead formed by press forming, and being used by pressing an apex of the bead onto a contact material.

Assignees

• Nisshin Steel Co Ltd

Inventors

• Matsubayashi Hiroyasu
• Nakamura Sadayuki
• Katsuki Junichi
• Hirota Ryoji

Classifications

• C22C38/42 Primary

  with copper · CPC title

• C22C38/54

  with boron · CPC title

• C22C38/06

  containing aluminium · CPC title

• C22C38/02

  containing silicon · CPC title

• C22C38/04

  containing manganese · CPC title