Structural polyurethane adhesive

Patent metadata

Field	Value
Publication number	US-10059863-B2
Application number	US-201314413371-A
Country	US
Kind code	B2
Filing date	Aug 26, 2013
Priority date	Aug 24, 2012
Publication date	Aug 28, 2018
Grant date	Aug 28, 2018

Abstract

A two-component polyurethane adhesive is described having high strength and extensibility, wherein the mechanical properties are only slightly dependent on the temperature. The polyurethane adhesive can be suitable as a structural adhesive. The adhesive can include a triol, a diol, a polyamine, a polyisocyanate, and a polyurethane polymer having isocayanate groups in certain ratios.

First claim

The invention claimed is:

1. A polyurethane adhesive comprising a first and a second component, wherein
the first component comprises
a) et least one triol A1 having a molecular weight in the range of 1,000 to 10,000 g/mol,
b) at least one diol A2 having two primary hydroxyl groups and a molecular weight in the range of 60 to 150 g/mol, and
c) at least one aliphatic polyamine A3 with a molecular weight in the range of 60 to 200 g/mol; and

the second component comprises
d) at least one polyisocyanate B1 and
e) at least one polyurethane polymer B2 having isocyanate groups, wherein B1 and B2 are not identical;

wherein said triol A1, said diol A2 and said polyamine A3 are present in such an amount that
f) ratio V1 of the number of OH groups and NH 2 groups of (A2+A3)/A1 is in the range of 4:1 to 10:1, and
g) ratio V2 of the number of OH groups and NH 2 groups of A2/A3 is in the range of 4:1 to 20:1.

2. The polyurethane adhesive according to claim 1 , wherein the triol is a polyether triol.

3. The polyurethane adhesive according to claim 1 , wherein the triol has primary hydroxyl groups.

4. The polyurethane adhesive according to claim 1 , wherein the diol is selected from the group consisting of 1,3-propanediol, 1,4-butanediol and 1,5-pentanediol.

5. The polyurethane adhesive according to claims 1 , wherein the polyamine is selected from the group consisting of 1,5-diamino-2-methylpentane, 2,2,4- and 2,4,4-trimethylhexamethylenediamine, 1,8-octanediamine, 1,10-decanediamine, 1,12-dodecanediamine, 1-amino-3-aminomethyl-3,5,5-trimethylcyclohexane, 2- and 4-methyl-1,3-diaminocyclohexane and mixtures thereof, 1,3-bis(aminomethyl)-cyclohexane, 1,4-bis(aminomethyl)-cyclohexane, 2,5(2,6)-bis(aminomethyl)bicyclo[2,2,1]heptane, 3(4),8(9) -bis(aminomethyl)tricyclo[5.2.1.0 2.6 ]decane, bis(2-aminoethyl)ether, 3,6-dioxaoctane -1,8-diamine, 4,7-dioxadecane-1,10-diamine, 4,7-dioxedecane-2,9-diamine, 4,9-dioxadodecane-1,12-diamine, 5,8-dioxadodecane-3,10-diamine, 1,3-bis(aminomethyl)benzene and 1,4-bis(aminomethyl)benzene.

6. The polyurethane adhesive according to claim 1 , wherein the ratio V1 is in the range of 5:1 to 9:1.

7. The polyurethane adhesive according to claim 1 , wherein the ratio V2 is in the range of 4.5:1 to 15:1.

8. The polyurethane adhesive according to claim 1 , wherein the polyisocyanate B 1 comprises a diphenylmethane diisocyanate (MDI) in the form of a 4,4′-MDI, a 2,4′-MDI, a 2,2′-MDI, or a mixture thereof.

9. The polyurethane adhesive according to claim 8 , wherein the polyisocyanate B1 comprises 50% to 95% by weight of MDI based on the weight of polyisocyanate B1.

10. The polyurethane adhesive according to claim 8 , wherein the polyisocyanate B 1 comprises 60 % to 90 % by weight of MDI based on the weight of polyisocyanate B1.

11. The polyurethane adhesive according to claim 1 , wherein the polyurethane polymer B2 has 50% to 95% by mass polyoxyalkylene units.

12. The polyurethane adhesive according to claim 1 , wherein the urethane groups and the free isocyanate groups of the polyurethane polymer B2 are derived from 4,4′-diphenylmethane diisocyanate.

13. A method for bonding a first substrate to a second substrate, the method comprising the steps of:
mixing of the two components of a polyurethane adhesive according to claim 1 ;
applying the mixed polyurethane adhesive to at least one of the substrate surfaces to be bonded:
joining the substrates to be bonded within the open time; and
curing the polyurethane adhesive.

14. The method according to claim 13 , wherein the preparation of the polyurethane polymer B2 does not take place in the presence of polyisocyanate B1.

15. The method according to claim 13 , wherein one or both substrates is or are a metal or a ceramic or a glass fiber-reinforced plastic or a carbon fiber-reinforced plastic.

16. An article obtained from a method of bonding according to claim 13 .

Assignees

• Sika Tech Ag
• Galderma Res & Dev

Inventors

• Roock Wolfgang
• Kelch Steffen
• Ittrich Florian
• Linnenbrink Martin

Classifications

• C08G18/12

  using two or more compounds having active hydrogen in the first polymerisation step · CPC title

• C09J175/04

  Polyurethanes · CPC title

• B32B7/12

  using interposed adhesives or interposed materials with bonding properties · CPC title

• B32B37/18

  involving the assembly of discrete sheets or panels only · CPC title

• C08G18/3206

  aliphatic · CPC title