Deformation of a polymer tube in the fabrication of a medical article

Patent metadata

Field	Value
Publication number	US-10058439-B2
Application number	US-201615282802-A
Country	US
Kind code	B2
Filing date	Sep 30, 2016
Priority date	Sep 30, 2004
Publication date	Aug 28, 2018
Grant date	Aug 28, 2018

Abstract

Methods of manufacturing a medical article that include radial deformation of a polymer tube are disclosed. A medical article, such as an implantable medical device or an inflatable member, may be fabricated from a deformed tube.

First claim

What is claimed is:

1. A method for fabricating a stent from a tube made from a polymer, comprising:
inducing crystallization in the tube comprising treating at least a portion of the tube with a solvent;
radially and axially deforming the tube including radially deforming the tube between 100% and 400% while the tube has a temperature equal to or above the glass transition temperature of the polymer of the tube; and
fabricating the stent from the deformed and treated tube including forming struts, wherein a strut has a straight portion and a curved portion.

2. The method of claim 1 , wherein inducing crystallization occurs before the deforming step and lowers the glass transition temperature of the polymer,
wherein the temperature during the radial and axial deformation is above the lowered glass transition temperature.

3. The method of claim 1 , wherein inducing crystallization modifies the radial strength of the deformed tube.

4. The method of claim 1 , wherein the tube is at least partially immersed in the solvent or spraying the tube with the solvent.

5. The method of claim 1 , wherein the solvent decreases a crystallization temperature of the polymer.

6. The method of claim 1 , wherein at least the portion of the tube is treated with the solvent prior to, contemporaneously with, and/or subsequent to deforming the tube.

7. The method of claim 1 , wherein the tube is cooled after the radial and axial deformation.

8. The method of claim 1 , wherein the polymer comprises poly (L-lactide).

9. The method of claim 1 , wherein the tube is heated prior to deforming the tube.

10. A method, comprising:
using a tube comprising a polymer;
inducing crystallization in the tube comprising treating at least a portion of the tube with a solvent;
radially and axially deforming the tube while the tube has a temperature equal to or above the glass transition temperature of the polymer of the tube, wherein the deformed and treated tube has a wall thickness of between 0.0025 inches and 0.006 inches; and
fabricating a stent from the deformed and treated tube, the stent comprising a network of interconnected struts, wherein a strut has a straight portion and a curved portion.

11. The method of claim 10 , wherein the deformed and treated tube has a wall thickness of between 0.0043 and 0.006 inches.

Assignees

• Abbott Cardiovascular Systems Inc

Inventors

• Huang Bin
• Durcan Jonathan P

Classifications

• B29C55/26 Primary

  biaxial · CPC title

• B29K2067/046

  PLA, i.e. polylactic acid or polylactide · CPC title

• B29K2995/006

  Bio-degradable, e.g. bioabsorbable, bioresorbable or bioerodible · CPC title

• A61F2/07

  Stent-grafts · CPC title

• A61F2002/91558

  connected peak to peak · CPC title