Bulk resin infusion

Patent metadata

Field	Value
Publication number	US-10052826-B2
Application number	US-201113279308-A
Country	US
Kind code	B2
Filing date	Oct 23, 2011
Priority date	Oct 25, 2005
Publication date	Aug 21, 2018
Grant date	Aug 21, 2018

Abstract

A method for performing resin infusion into a dry reinforcement on a layup mandrel comprises placing resin at a resin zone on the mandrel; bagging the reinforcement and the resin with a bagging film; heating the resin while applying compaction pressure to the bagging film to cause the resin to be infused into the reinforcement; and creating a pressure differential outside of the bagging film over the resin zone to control rate and pressure at which the resin is infused into the reinforcement. As a result, the resin pressure and infusion rate are controlled independently of the compaction pressure on the reinforcement.

First claim

The invention claimed is:

1. A method for performing resin infusion into a dry reinforcement on a layup mandrel, the method comprising:
placing resin at a resin zone on the layup mandrel;
bagging the reinforcement and the resin with a bagging film;
heating the resin while applying compaction pressure to the bagging film to cause the resin to be infused into the reinforcement; and
creating a pressure differential outside of the bagging film over the resin zone to control rate and pressure at which the resin is infused into the reinforcement;
whereby the resin pressure and infusion rate are controlled independently of the compaction pressure on the reinforcement.

2. The method of claim 1 , wherein the rate of the infusion is controlled by modulating the pressure differential.

3. The method of claim 1 , wherein a vacuum cup is used to create the pressure differential over the resin zone.

4. The method of claim 3 , further comprising sealing the vacuum cup to an outside of the bagging film over the resin zone.

5. The method of claim 3 , wherein the vacuum cup includes a chamber that is placed over the resin zone, and wherein pressure within the chamber is modulated during the resin infusion.

6. The method of claim 5 , wherein pressure in the chamber exceeds pressure within the bagging film during resin infusion.

7. The method of claim 5 , wherein an autoclave is used to heat the resin and increase ambient pressure on the bagging film; and wherein the chamber pressure is higher than standard atmospheric pressure during resin infusion.

8. The method of claim 7 , wherein the pressure differential is passively controlled so that vacuum cup pressure automatically maintains a fixed pressure differential to the ambient pressure outside the bagging film.

9. The method of claim 3 , wherein infusion media is used to transport resin from the resin zone to the reinforcement; and wherein a scalloped area of the vacuum cup is used to concentrate force on adjacent areas of the infusion media as the resin flows from the resin zone to the infusion media.

10. The method of claim 1 , further comprising placing infusion media above the resin so the bagging film pushes the infusion media down into the resin to begin the resin infusion.

11. The method of claim 1 , wherein the resin is disposed in contact with infusion media, which is adjacent to the reinforcement.

12. The method of claim 1 , wherein the resin is solid or putty-like.

13. A method comprising performing bulk resin infusion of resin into a reinforcement starting with resin at a starting location underneath an envelope, wherein ambient pressure around a portion of the envelope that covers the resin is modulated relative to ambient pressure around a portion of the envelope that covers the reinforcement to control resin pressure and infusion rate independently of compaction pressure on the reinforcement, wherein out gassing of the resin is performed prior to resin infusion, and wherein the out gassing includes applying a lower-than-ambient pressure outside of the envelope over the resin starting location to lift the envelope off the resin and thereby create a volume through which gasses may escape prior to infusion.

14. The method of claim 13 , wherein a vacuum cup including a chamber is placed on the envelope over the resin starting location, and wherein pressure within the chamber is controlled relative to the pressure within the envelope to facilitate the resin infusion.

15. The method of claim 13 , wherein an autoclave is used to heat the resin and increase ambient pressure on the envelope; and wherein a chamber pressure is higher than standard atmospheric pressure during resin infusion.

16. The method of claim 13 , wherein infusion media is placed above the resin prior to the resin infusion so the envelope pushes the infusion media down into the resin to begin the resin infusion.

17. A method for performing resin infusion into a dry reinforcement on a layup mandrel, the method comprising:
placing resin at a resin zone on the layup mandrel;
bagging the reinforcement and the resin with a bagging film;
heating the resin while applying compaction pressure to the bagging film to cause the resin to be infused into the reinforcement; and
creating a pressure differential outside of the bagging film over the resin zone to control rate and pressure at which the resin is infused into the reinforcement;
whereby the resin pressure and infusion rate are controlled independently of the compaction pressure on the reinforcement;
wherein out gassing of the resin is performed prior to resin infusion, the out gassing includes applying a lower-than-ambient pressure outside of the bagging film over the resin zone to lift the bagging film off the resin and thereby create a volume through which gasses can escape prior to infusion.

18. The method of claim 17 , wherein the rate of the infusion is controlled by modulating the pressure differential.

19. The method of claim 17 , wherein a vacuum cup is used to create the pressure differential over the resin zone.

20. The method of claim 19 , further comprising sealing the vacuum cup to an outside of the bagging film over the resin zone.

Assignees

• Hawkins Robert Dennis
• Boeing Co

Inventors

• Hawkins Robert Dennis

Classifications

• B29C70/465

  and impregnating by melting a solid material, e.g. sheets, powders of fibres · CPC title

• B29L2031/779

  Heating equipment · CPC title

• B29C70/443

  and impregnating by vacuum or injection · CPC title

• B29C70/342 Primary

  using isostatic pressure · CPC title

• B29C70/549

  Details of caul plates, e.g. materials or shape · CPC title