Gypsum composition for refractory moulds

Patent metadata

Field	Value
Publication number	US-10052680-B2
Application number	US-201314404545-A
Country	US
Kind code	B2
Filing date	May 27, 2013
Priority date	May 30, 2012
Publication date	Aug 21, 2018
Grant date	Aug 21, 2018

Abstract

The invention relates to a mineral composition for the preparation of foundry molds, comprising:
(a) from 20% to 90% by weight of plaster, (b) from 10% to 80% by weight of a mineral component based on silica and/or alumina, and (c) from 0.5% to 4.8%, preferably from 1.5% to 4.5% and in particular between 2% and 4.5% by weight, of a mineral powder having a thermal conductivity (λ), at 20° C., of greater than 15 W/(m·K) and a specific surface area of greater than 10 m 2 /g, these percentages being relative to the total weight of the sum of the components (a), (b) and (c).

First claim

The invention claimed is:

1. A mineral composition, comprising, relative to a total combined weight of components (a), (b), and (c):
(a) from 33% to 89.5% by weight of plaster,
(b) from 10% to 66.5% by weight of a mineral component based on silica and/or alumina, and
(c) from 0.5% to 4.8% by weight of a mineral powder having a thermal conductivity (λ) at 20° C. from 15 to 500 W/(m·K) and a BET specific surface area from 10 to 50 m 2 /g, wherein the mineral powder is selected from the group consisting of graphite, zinc oxide, silicon carbide, boron carbide, zirconium carbide, tungsten carbide, titanium nitride, aluminium nitride, gallium nitride, indium nitride, nickel, iron, and copper,
wherein the composition is suitable for preparation of a foundry mold.

2. The mineral composition according to claim 1 , wherein the mineral powder (c) has a thermal conductivity (λ) at 20° C. of between 20 and 500 W/(m·K).

3. The mineral composition according to claim 1 , wherein the mineral powder (c) is a graphite powder.

4. The mineral composition according to claim 1 , wherein the median diameter (D 50 ) of the mineral powder (c), determined by laser particle size analysis, is between 5 and 250 μm.

5. The mineral composition according to claim 1 , wherein the BET specific surface area of the mineral powder (c) is between 12 and 50 m 2 /g.

6. The mineral composition according to claim 1 , wherein the mineral powder (c) has a bulk density of between 0.02 and 0.3 g/cm 3 .

7. The mineral composition according to claim 1 , wherein the mineral component (b) based on silica and/or alumina is at least one component selected from the group consisting of silica, alumina, cordierite, and a refractory chamotte based on mullite.

8. The mineral composition according to claim 1 , further comprising:
at least one other additive selected from the group consisting of expanded glass beads, unexpanded glass beads, glass flakes, mineral fibers, and vermiculite,
wherein the at least one other additive is present in an amount up to 30% relative to the total combined weight of components (a), (b), and (c).

9. A process for manufacturing a foundry mould, the process comprising:
mixing the mineral composition according to claim 1 with water, thereby obtaining a fluid composition,
casting the fluid composition in a mold comprising a model of a part to be moulded, thereby obtaining a casted composition,
setting the casted composition and, after complete curing,
removing the model or separating the model and the mold.

10. A foundry mold obtained by a process comprising the process of claim 9 .

11. The foundry mold according to claim 10 , wherein the mold has a thermal diffusivity at ambient temperature of between 0.2 and 2 mm 2 /s.

12. The mineral composition according to claim 1 , comprising from 30% to 66.5% of the mineral component (b), relative to the total weight of the sum of components (a), (b) and (c).

13. The mineral composition according to claim 1 , comprising from 40% to 66.5% of the mineral component (b), relative to the total weight of the sum of components (a), (b) and (c).

14. The mineral composition according to claim 1 , comprising from 1.5% to 4.5% of the mineral powder (c), relative to the total weight of the sum of components (a), (b) and (c).

15. The mineral composition according to claim 1 , comprising from 2% to 4.5% of the mineral powder (c), relative to the total weight of the sum of components (a), (b) and (c).

16. The mineral composition according to claim 3 , wherein the graphite powder is an expanded graphite powder.

17. The mineral composition according to claim 3 , wherein the graphite powder is a compacted expanded graphite powder.

Assignees

• Saint Gobain Placo

Inventors

• Retot Helene
• Petigny Nathalie
• Fourdrin Emmanuel
• Thioliere Stephane

Classifications

• C04B2111/00939

  for the fabrication of moulds or cores · CPC title

• B22C1/181

  Cements, oxides or clays · CPC title

• C04B28/146

  alpha-hemihydrate · CPC title

• B22C1/00 Primary

  Compositions of refractory mould or core materials; Grain structures thereof (refractory materials in general C04B35/00); Chemical or physical features in the formation or manufacture of moulds · CPC title

• B22C9/02

  Sand moulds or like moulds for shaped castings · CPC title