Solid electrolyte laminate, method for manufacturing solid electrolyte laminate, and fuel cell

Patent metadata

Field	Value
Publication number	US-10050295-B2
Application number	US-201314387635-A
Country	US
Kind code	B2
Filing date	Mar 26, 2013
Priority date	Mar 28, 2012
Publication date	Aug 14, 2018
Grant date	Aug 14, 2018

Abstract

Provided is a solid electrolyte laminate comprising a solid electrolyte layer having proton conductivity and a cathode electrode layer laminated on one side of the solid electrolyte layer and made of lanthanum strontium cobalt oxide (LSC). Also provided is a method for manufacturing the solid electrolyte. This solid electrolyte laminate can further comprise an anode electrode layer made of nickel-yttrium doped barium zirconate (Ni—BZY). This solid electrolyte laminate is suitable for a fuel cell operating in an intermediate temperature range less than or equal to 600° C.

First claim

The invention claimed is:

1. A solid electrolyte laminate comprising:
a solid electrolyte layer having proton conductivity; and
a cathode electrode layer laminated on one side of said solid electrolyte layer and made of lanthanum strontium cobalt oxide (LSC),
wherein said solid electrolyte layer is formed from yttrium-doped barium zirconate (BZY), and
a doped amount of yttrium is 15 mol % to 20 mol %, and
wherein the rate of increase in lattice constant of said solid electrolyte layer at 100° C. to 1000° C. with respect to temperature changes is 3.3×10 −5 Å/° C. to 4.3×10 −5 Å/° C., and a rate of increase in lattice constant at 200° C. to 400° C. with respect to temperature changes being 3.3×10 −5 Å/° C. to 4.3×10 −5 Å/° C.,
wherein said yttrium-doped barium zirconate (BZY) is a polycrystalline substance containing a plurality of crystal grains, and a mean diameter of said crystal grains is more than or equal to 1 μm.

2. The solid electrolyte laminate according to claim 1 , wherein the lattice constant of said solid electrolyte layer at room temperature is 4.218 Å to 4.223 Å.

3. The solid electrolyte laminate according to claim 1 , wherein proton conductivity of said solid electrolyte layer at 400° C. to 800° C. is 1 mS/cm to 60 mS/cm.

4. The solid electrolyte laminate according to claim 1 , further comprising an anode electrode layer laminated on the other side of said solid electrolyte layer and made of nickel-yttrium doped barium zirconate (Ni—BZY).

5. A fuel cell comprising the solid electrolyte laminate as defined in claim 1 .

6. A method for manufacturing the solid electrolyte laminate as defined in claim 1 , comprising:
a first grinding step of mixing and grinding BaCO 3 , ZrO 2 and Y 2 O 3 to obtain a first mixture;
a first heat treatment step of heat treating said first mixture;
a second grinding step of grinding the first mixture having undergone said first heat treatment step again to obtain a second mixture;
a first compression molding step of compression molding said second mixture to obtain a first compact;
a second heat treatment step of heat treating said first compact;
a third grinding step of grinding the first compact having undergone said second heat treatment step to obtain a ground product;
a second compression molding step of compression molding said ground product to obtain a second compact;
a solid electrolyte sintering step of heat treating said second compact at a temperature of 1400° C. to 1600° C. for at least 20 hours in an oxygen atmosphere to obtain a sintered compact;
a third heat treatment step of holding said sintered compact at a temperature lower than in said solid electrolyte sintering step;
a cathode electrode material laminating step of laminating an electrode material made of said lanthanum strontium cobalt oxide (LSC) on one side of the sintered compact having undergone said third heat treatment step;
an anode electrode material laminating step of laminating an electrode material made of nickel-yttrium doped barium zirconate (Ni—BZY) on the other side of the sintered compact having undergone said third heat treatment step; and
an electrode material sintering step of heating the sintered compact with said electrode materials laminated thereon to or above a sintering temperature of said electrode materials.

7. The method for manufacturing the solid electrolyte laminate according to claim 6 , wherein said third heat treatment step is carried out by holding at a temperature of 400° C. to 1000° C. for 5 hours to 30 hours.

8. A method for manufacturing the solid electrolyte laminate as defined in claim 1 , comprising:
an anode electrode material preparing step of mixing BaCO 3 , ZrO 2 , Y 2 O 3 , and Ni;
an anode electrode molding step of compression molding an anode electrode material to form an anode electrode compact to be an anode electrode layer;
a first grinding step of mixing and grinding BaCO 3 , ZrO 2 and Y 2 O 3 to obtain a first mixture;
a first heat treatment step of heat treating said first mixture;
a second grinding step of grinding the first mixture having undergone said first heat treatment step again to obtain a second mixture;
a first compression molding step of compression molding said second mixture to obtain a compact;
a second heat treatment step of heat treating said compact;
a third grinding step of grinding the compact having undergone said second heat treatment step to obtain a ground product;
a paste forming step of forming said ground product into paste to obtain paste;
a solid electrolyte laminating step of laminating said paste on one side of said anode electrode compact to obtain a first laminate including a thin-film solid electrolyte layer;
an anode electrode-solid electrolyte sintering step of heat treating said first laminate at a temperature of 1400° C. to 1600° C. for at least 20 hours in an oxygen atmosphere;
a third heat treatment step of holding the first laminate having undergone said anode electrode-solid electrolyte sintering step at a temperature lower than in said anode electrode-solid electrolyte sintering step;
a cathode electrode material laminating step of laminating a cathode electrode material made of said lanthanum strontium cobalt oxide (LSC) on one side of the solid electrolyte layer included in the first laminate having undergone said third heat treatment step to obtain a second laminate; and
a cathode electrode sintering step of heating said second laminate to or above a sintering temperature of said cathode electrode material.

9. The method for manufacturing the solid electrolyte laminate according to claim 8 , wherein said third heat treatment step is carried out after cooling the first laminate having undergone said anode electrode-solid electrolyte sintering step to ordinary temperature.

10. The method for manufacturing the solid electrolyte laminate according to claim 8 , wherein said anode electrode-solid electrolyte sintering step and said third heat treatment step are carried out sequentially.

Assignees

• Sumitomo Electric Industries
• Univ Kyoto

Inventors

• Hiraiwa Chihiro
• Majima Masatoshi
• Yamaguchi Atsushi
• Mizuhara Naho
• Uda Tetsuya
• Noda Yohei

Classifications

• C04B35/48 Primary

  based on zirconium or hafnium oxides, zirconates, {zircon} or hafnates · CPC title

• C04B35/486

  Fine ceramics · CPC title

• H01M8/1253 Primary

  the electrolyte containing zirconium oxide · CPC title

• H01M4/9033

  Complex oxides, optionally doped, of the type M1MeO3, M1 being an alkaline earth metal or a rare earth, Me being a metal, e.g. perovskites · CPC title

• H01M2300/0071

  Oxides · CPC title