Vinyl-based thermoplastic resin composition, method for manufacturing thereof and vinyl-based thermoplastic resin manufactured therefrom

Patent metadata

Field	Value
Publication number	US-10047180-B2
Application number	US-201515105983-A
Country	US
Kind code	B2
Filing date	Oct 7, 2015
Priority date	Oct 8, 2014
Publication date	Aug 14, 2018
Grant date	Aug 14, 2018

Abstract

The present invention relates to vinyl-based thermoplastic resin composition having excellent thermal stability, which comprises a metal complex agent, and a first vinyl-based monomer and a second vinyl-based monomer having different iron ion concentration from each other, a method for manufacturing thereof, and vinyl-based thermoplastic resin manufactured therefrom. The accompanying vinyl-based thermoplastic resin composition can enhance thermal stability, and the vinyl-based thermoplastic resin manufactured from the composition may have excellent thermal stability. Thus, it can be easily applied to industries requiring thereof, in particular, industries of vinyl-based thermoplastic resin and its mold processed goods.

First claim

The invention claimed is:

1. Vinyl-based thermoplastic resin composition comprising a metal complex agent 0.05 part by weight to 0.5 part by weight, based on a monomer mixture 100 parts by weight,
wherein the monomer mixture comprises a first vinyl-based monomer and a second vinyl-based monomer,
wherein the first vinyl-based monomer and the second vinyl-based monomer contain iron ions of different concentration from each other, and
wherein the second vinyl-based monomer has 100 folds to 300 folds higher iron ion concentration than the iron ion concentration in the first vinyl-based monomer.

2. The vinyl-based thermoplastic resin composition of claim 1 , wherein the monomer mixture comprises the first vinyl-based monomer and the second vinyl-based monomer at weight ratio of 1.2 to 1.8:1.

3. The vinyl-based thermoplastic resin composition of claim 1 , wherein the second vinyl-based monomer has iron ion concentration of 5 ppm to 30 ppm.

4. The vinyl-based thermoplastic resin composition of claim 1 , wherein the metal complex agent is at least one selected from the group consisting of a phosphoric acid-based compound, an alkali metal phosphate-based compound, an aminocarboxylic acid-based compound and an oxycarboxylic acid-based compound.

5. The vinyl-based thermoplastic resin composition of claim 4 , wherein the phosphoric acid-based compound is at least one selected from the group consisting of pyrophosphoric acid, tripolyphosphoric acid, pentapolyphosphoric acid, trimetaphosphoric acid, tetrametaphosphoric acid and hexametaphosphoric acid.

6. The vinyl-based thermoplastic resin composition of claim 4 , wherein the alkali metal phosphate-based compound is at least one selected from the group consisting of disodium pyrophosphate, trisodium pyrophosphate, tetra-sodium pyrophosphate and potassium pyrophosphate.

7. The vinyl-based thermoplastic resin composition of claim 4 , wherein the aminocarboxylic acid-based compound is at least one selected from the group consisting of ethylenediamine-N-monoacetic acid, ethylenediamine-N,N′-diacetic acid and ethylenediamine-N,N,N′,N′-tetraacetic acid.

8. The vinyl-based thermoplastic resin composition of claim 4 , wherein the oxycarboxylic acid-based compound is at least one selected from the group consisting of glycolic acid, gluconic acid, lactic acid, glyceric acid, tartaric acid, malic acid, salicylic acid, gallic acid and citric acid.

9. The vinyl-based thermoplastic resin composition of claim 1 , wherein the metal complex agent is at least one selected from the following compounds expressed by Chemical Formulas 1 to 3:

in the Chemical Formula 1, Chemical Formula 2 and Chemical Formula 3,
wherein the R 1 to the R 5 are each independently C 1-10 alkyl, C 1-10 halogenated alkyl, C 1-10 aryl or C 1-10 halogenated aryl.

10. A method for manufacturing vinyl-based thermoplastic resin composition by mass polymerization comprising:
a pre-polymerization step of manufacturing a particle core by polymerizing a first vinyl-based monomer, a second vinyl-based monomer and a pre-polymerization initiator; and
a post-polymerization step of adding the first vinyl-based monomer, the second vinyl-based monomer and a post-polymerization initiator to the particle core and then polymerizing thereof,
wherein a metal complex agent is inserted in the pre-polymerization step, or the pre-polymerization step and the post-polymerization step, and
wherein the second vinyl-based monomer has 100 folds to 300 folds higher iron ion concentration than the iron ion concentration in the first vinyl-based monomer.

11. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the second vinyl-based monomer has iron ion concentration of 5 ppm to 30 ppm.

12. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the metal complex agent is inserted in bulk in the pre-polymerization step.

13. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein a part of the metal complex agent is inserted in the pre-polymerization step, and the rest of the metal complex agent is inserted in the post-polymerization step.

14. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the metal complex agent is inserted in an amount of 0.05 part by weight to 0.5 part by weight, based on the total 100 parts by weight of the first vinyl-based monomer and the second vinyl-based monomer.

15. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the metal complex agent is at least one selected from the group consisting of a phosphoric acid-based compound, an alkali metal phosphate-based compound, an aminocarboxylic acid-based compound and an oxycarboxylic acid-based compound.

16. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the metal complex agent is at least one selected from the following compounds expressed by Chemical Formulas 1 to 3:

in the Chemical Formula 1, Chemical Formula 2 and Chemical Formula 3,
wherein the R 1 to the R 5 are each independently C 1-10 alkyl, C 1-10 halogenated alkyl, C 1-10 aryl or C 1-10 halogenated aryl.

17. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the pre-polymerization initiator is used in an amount of 0.05 part by weight to 1 part by weight, based on the total 100 parts by weight of the first vinyl-based monomer and the second vinyl-based monomer of the pre-polymerization step.

18. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the post-polymerization initiator is used in an amount of 0.05 part by weight to 1 part by weight, based on the total 100 parts by weight of the first vinyl-based monomer and the second vinyl-based monomer of the pre-polymerization step.

19. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the pre-polymerization initiator and the post-polymerization initiator are materials having half-life of 1 hour at a temperature range of 55° C. to 70° C.

20. The method for manufacturing vinyl-based thermoplastic resin composition of claim 19 , wherein the pre-polymerization initiator and the post-polymerization initiator are each independently cumyl peroxyneodecanoate, 1,1,3,3,-tetramethyl butyl peroxyneodecanoate, t-hexyl peroxyneodecanoate, t-butyl peroxyneodecanoate, t-hexyl peroxypivalate, t-butyl peroxypivalate, di-sec-butyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, isobutyryl peroxide, 3,5,5-trimethylhexanoyl peroxide and lauryl peroxide.

21. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the pre-polymerization is conducted under conditions of reaction pressure of 9.5 K/G to 12.5 K/G and reaction temperature of 40° C. to 80° C.

22. The method for manufacturing vinyl-based thermoplastic resin composition of claim 10 , wherein the post-polymerization is conducted under conditions of reaction pressure of 7.5 K/G to 8.5 K/G and reaction temperature of 60° C. to 80° C.

23. The met

Assignees

• Lg Chemical Ltd

Inventors

• Lee Se Woong
• Ahn Seong Yong
• Kim Kun Ji
• Kim Kyung Hyun

Classifications

• C08G85/002

  Post-polymerisation treatment · CPC title

• C08K3/32

  Phosphorus-containing compounds · CPC title

• C08K5/07

  Aldehydes; Ketones · CPC title

• C08F214/06 Primary

  Vinyl chloride · CPC title

• C08F214/00

  Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen · CPC title