Method for smelting nickel oxide ore

Patent metadata

Field	Value
Publication number	US-10041144-B2
Application number	US-201515328634-A
Country	US
Kind code	B2
Filing date	Jun 30, 2015
Priority date	Aug 1, 2014
Publication date	Aug 7, 2018
Grant date	Aug 7, 2018

Abstract

Provided is a method for smelting nickel oxide ore by which the occurrence of cracking due to heat shock can be suppressed when nickel oxide ore is pelletized and charged into a smelting step (reduction step). A method for smelting nickel oxide ore according to the present invention uses pellets of nickel oxide ore, the method being characterized by comprising a pellet production step S 1 for producing pellets from nickel oxide ore, and a reduction step S 2 for heating the resulting pellets at a predetermined reduction temperature in a reduction furnace, the reduction step S 2 comprising preheating the pellets obtained in the pellet production step S 1 to a temperature of 350 to 600° C. in the reduction furnace and thereafter charging the pellets into the reduction furnace and raising the temperature of the reduction furnace to the reduction temperature.

First claim

The invention claimed is:

1. A method for smelting nickel oxide ore using pellets of nickel oxide ore, the method comprising:
a pellet production step of producing pellets from the nickel oxide ore; and
a reduction step of conducting a reducing process that heats the pellets obtained at a predetermined reduction temperature with a reducing furnace,
wherein the pellets are produced in the pellet production step by conducting heat treatment on a lump made by forming the nickel oxide ore into an aggregate form by holding at a temperature of 100° C. to 170° C. for 2 hours or more in an apparatus different from the reducing furnace, and the size of the pellets produced from the nickel oxide ore in the pellet production step is on the order of 10 mm to 30 mm in size, and
wherein the pellets obtained in the pellet production step are charged into the reducing furnace, and the pellets are heated in the reducing furnace to 400° C. to 550° C. before reduction begins.

Assignees

• Sumitomo Metal Mining Co

Inventors

• Takahashi Junichi
• Inoue Taku
• Okada Shuuji

Classifications

• C22B1/245 Primary

  with carbonaceous material for the production of coked agglomerates · CPC title

• C22B5/10

  by solid carbonaceous reducing agents · CPC title

• C22B23/02

  by dry processes · CPC title

• C22B1/2413

  enduration of pellets · CPC title

• C22B23/005

  Preliminary treatment of ores, e.g. by roasting or by the Krupp-Renn process · CPC title