Abstract

The objectionable odor of one component condensation curable organopolysiloxane compositions is eliminated by replacing all or the most substantial part of water scavenger vinyltrimethoxysilane with a phenyltrialkoxysilane, without compromising storage or curing properties.

First claim

What is claimed is:

1. A crosslinkable composition, comprising:
(A) an alkoxysilyl-terminated, crosslinkable polymer component, consisting essentially of 100 parts by weight of at least one compound of the formula
Y—[(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] x   (I),

where
Y is an x-valent polymeric moiety attached via nitrogen, oxygen, sulfur or carbon,
R at each occurrence are the same or different and are monovalent, optionally substituted hydrocarbyl moieties,
R 1 at each occurrence are the same or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl moiety, which is attached to the carbon atom via nitrogen, phosphorus, oxygen, sulfur or a carbonyl group,
R 2 at each occurrence are the same or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl moiety,
x is an integer from 1 to 10,
a at each occurrence are the same or different and are 0, or 1, and
b at each occurrence are the same or different and are an integer from 1 to 10,
(B) 0.2 to 50 parts by weight of a phenyltrialkoxysilane of the formula
C 6 H 5 —Si(OR 3 ) 3   (II),

where
R 3 at each occurrence are the same or different and are methyl or ethyl,
(C) 0.1 to 30 parts by weight of a nitrogenous organosilicon compound containing a unit of the formula
D e Si(OR 5 ) d R 4 c O (4-e-d-c)/2   (III),

where
R 4 at each occurrence are the same or different and are monovalent, optionally substituted, SiC-bonded organic moieties free of nitrogen,
R 5 at each occurrence are the same or different and are hydrogen or an optionally substituted hydrocarbyl moiety,
D at each occurrence are the same or different and are monovalent SiC-bonded moieties having at least one nitrogen atom not bonded to a carbonyl group (C═O),
c is 0, 1, 2 or 3,
d is 1, 2 or 3, and
e is 0, 1, 2, 3 or 4,
with the proviso that the c+d+e sum is not more than 4 and at least one D moiety is present per molecule,
wherein the crosslinkable composition contains less than 0.5 wt % of vinyltrimethoxysilane, based on the total weight of the crosslinkable composition.

2. The crosslinkable composition of claim 1 , wherein the Y moiety comprises polyurethane moieties or polyoxyalkylene moieties.

3. The crosslinkable composition of claim 1 , wherein component (B) is phenyltrimethoxysilane.

4. The crosslinkable composition of claim 1 , wherein the composition contains less than 0.3 wt % of vinyltrimethoxysilane, based on the total weight of the composition.

5. The crosslinkable composition of claim 1 , wherein the composition contains component (B) in an amount of 0.5 to 50 parts by weight, based on 100 parts by weight of component (A).

6. The crosslinkable composition of claim 1 , comprising:
(A) 100 parts by weight of a compound of formula (I),
(B) 0.5 to 50 parts by weight of phenyltrimethoxysilane,
(C) 0.2 to 25 parts by weight of a nitrogenous organosilicon compound containing a unit of formula (III),
(D) optionally a plasticizer,
(E) optionally a filler,
(F) optionally an adhesion promoter,
(G) optionally a phenylsilicone resin,
(H) optionally a catalyst,
(I) optionally an additive, and
(J) optionally an admixture agent,

wherein the composition contains less than 0.3 wt % of vinyltrimethoxysilane, based on the total weight of the composition.

7. The crosslinkable composition of claim 1 , comprising:
(A) 100 parts by weight of a compound of formula (I),
(B) 0.8 to 30 parts by weight of phenyltrimethoxysilane,
(C) 0.3 to 20 parts by weight of a nitrogenous organosilicon compound containing a unit of formula (III),
(D) optionally a plasticizer,
(E) optionally 50 to 500 parts by weight of a filler,
(F) optionally an adhesion promoter,
(G) optionally a phenylsilicone resin,
(H) optionally a catalyst,
(I) optionally an additive, and
(J) optionally an admixture agent,

wherein the composition contains less than 0.1 wt % of vinyltrimethoxysilane, based on the total weight of the composition.

8. A method of forming a composition of claim 1 , comprising mixing the individual components in any order.

9. A shaped article obtained by crosslinking a composition of claim 1 .

10. A method of forming a composite, comprising applying applying a composition of a claim 1 to a substrate and then crosslinking the compostion.

11. The crosslinkable composition of claim 1 , wherein a is 0 in at least one compound of the formula (II).

12. The crosslinkable composition of claim 1 , wherein all alkoxysilyl-terminated, crosslinkable polymers are of the formula (II) where a is 0.

13. A crosslinkable composition, comprising:
(A) an alkoxysilyl-terminated, crosslinkable polymer component, consisting of 100 parts by weight of at least one compound of the formula
Y—[(C 1 2 ) b —SiR a (OR 2 ) 3-a ] x   (I)

where
Y is an x-valent polymeric moiety attached via nitrogen, oxygen, sulfur or carbon,
R at each occurrence are the same or different and are monovalent, optionally substituted hydrocarbyl moieties,
R l at each occurrence are the same or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl moiety, which is attached to the carbon atom via nitrogen, phosphorus, oxygen, sulfur or a carbonyl group,
R 2 at each occurrence are the same or different and are hydrogen or a monovalent, optionally substituted hydrocarbyl moiety,
x is an integer from 1 to 10,
a at each occurrence are the same or different and are 0, or 1, and
b at each occurrence are the same or different and are an integer from 1 to 10,
(B) 0.2 to 50 part by weight of a phenyltrialkoxysilane of the formula
C 6 H 5 —Si(OR 3 ) 3   (II),

where
R 3 at each occurrence are the same or different and are methyl or ethyl,
(C) 0.1 to 30 parts by weight of a nitrogenous organosilicon compound containing a unit of the formula
D e Si(OR 5 ) d R 4 c O (4-e-d-c)/2   (III)

where
R 4 at each occurrence are the same or different and are monovalent, optionally substituted, SiC-bonded organic moieties free of nitrogen,
R 5 at each occurrence are the same or different and are hydrogen or an optionally substituted hydrocarbyl moiety,
D at each occurrence are the same or different and are monovalent SiC-bonded moieties having at least one nitrogen atom not bonded to a carbonyl group (C═O),
c is 0, 1, 2 or 3,
d is 1, 2 or 3, and
e is 0, 1, 2, 3 or 4,
with the proviso that the c+d+e sum is not more than 4 and at least one D moiety is present per molecule,
wherein the crosslinkable composition contains less than 0.5 wt% of vinyltrimethoxysilane, based on the total weight of the crosslinkable composition.

Assignees

• Wacker Chemie Ag

Inventors

• Stanjek Volker
• Bauer Andreas
• Zander Lars

Classifications

• C08G77/80

  Siloxanes having aromatic substituents, e.g. phenyl side groups · CPC title

• C09D183/12

  containing polyether sequences · CPC title

• C08G77/46

  containing polyether sequences · CPC title

• C08K2201/003

  Additives being defined by their diameter · CPC title

• C09J183/12

  containing polyether sequences · CPC title