Methods to texture opaque, colored and translucent materials

Patent metadata

Field	Value
Publication number	US-10040718-B2
Application number	US-201314438755-A
Country	US
Kind code	B2
Filing date	Oct 30, 2013
Priority date	Nov 2, 2012
Publication date	Aug 7, 2018
Grant date	Aug 7, 2018

Abstract

Methods of modifying glass-ceramic articles and glass-ceramic articles formed therefrom. The methods include providing a glass-ceramic article having a non-damaged surface, applying a chemical etching solution to the non-damaged surface, and removing the chemical etching solution. The chemical etching solution modifies the non-damaged surface so that from about 0.01 μm to about 2 μm of a depth of the glass-ceramic article is removed. The chemical etching solution modifies the non-damage surface of the glass-ceramic article to form a roughened surface having a reduced gloss value and a target roughness value.

First claim

What is claimed is:

1. A method of modifying a non-damaged surface of a glass-ceramic article, the method comprising:
a) providing a glass-ceramic article having a non-damaged surface and an initial gloss value;
b) applying a chemical etching solution to the non-damaged surface of the glass-ceramic article for an etching time of about 5 s to less than 15 min to form a roughened surface, remove from about 0.01 μm to about 20 μm of depth of the glass-ceramic article and reduce the initial gloss value to a reduced gloss value from about 10% to 70% at 60°, wherein the chemical etching solution is formed by mixing hydrofluoric acid and an inorganic fluoride salt, the concentration of hydrofluoric acid is from 1% to 6% by weight of the etching solution and the inorganic fluoride salt is 5% to 30% by weight of the etching solution; and
c) removing the chemical etching solution from the roughened surface.

2. The method of claim 1 , wherein the inorganic fluoride salt is selected from the group consisting of ammonium fluoride, ammonium bifluoride, buffered hydrofluoric acid, sodium fluoride, sodium bifluoride, potassium fluoride, potassium bifluoride, and combinations thereof.

3. The method of claim 1 , wherein the chemical etching solution further comprises a mineral acid selected from the group consisting of hydrochloric acid, nitric acid, phosphoric acid, sulfuric acid, boric acid, hydrofluoric acid, hydrobromic acid, perchloric acid, and combinations thereof and optionally further comprises an organic acid.

4. The method of claim 1 , wherein the chemical etching solution further comprises a wetting agent selected from the group consisting of glycols, glycerols, alcohols, surfactants, and combinations thereof.

5. The method of claim 1 , wherein the chemical etching solution further comprises a thickening agent.

6. The method of claim 1 , wherein the etching time is from about 1 min to about 8 min.

7. The method of claim 1 , wherein the chemical etching solution modifies the non-damaged surface such that from about 0.25 μm to about 1 μm of the depth of the glass-ceramic article is removed.

8. The method of claim 1 , wherein the reduced gloss value is from about 10% to about 60% at 60°, and wherein the chemical etching solution is applied to the non-damaged surface after the glass-ceramic article is subjected to ion exchange.

9. The method of claim 1 , wherein the reduced gloss value is from about 10% to about 30% at 60°.

10. The method of claim 1 , wherein the surface is roughened to a target roughness value from about 10 RMS (nm) to about 1000 RMS (nm), and wherein formation of the roughened surface having the reduced gloss value and the target roughness value preserves and/or improves surface strength of the glass-ceramic article.

11. The method of claim 10 , wherein the target roughness value is from about 150 RMS (nm) to about 800 RMS (nm).

12. The method of claim 1 , wherein the glass-ceramic article comprises a major crystalline phase.

13. The method of claim 12 , wherein the reduced gloss value is from about 10% to about 30% at 60°; and the chemical etching solution modifies the non-damaged surface such that from about 0.1 μm to about 2 μm of the depth of the glass-ceramic article is removed.

14. The method of claim 1 , wherein the glass-ceramic article comprises a major amorphous phase.

15. The method of claim 14 , wherein: the chemical etching solution comprises from about 5% to about 25% ammonium bifluoride as the mixture of hydrofluoric acid and the inorganic fluoride salt; the chemical etching solution further comprises from about 5% to about 25% of a wetting agent; the reduced gloss value is from about 10% to about 30% at 60°; and the etching time is from about 1 min to about 4 min.

16. A method of modifying a non-damaged surface of a glass-ceramic article having a major amorphous phase, the method comprising:
a) providing a glass-ceramic article having a non-damaged surface and an initial gloss value;
b) applying a chemical etching solution to the non-damaged surface of the glass-ceramic article for an etching time of about 5 s to less than 15 min to form a roughened surface having a target roughness value of from about 150 RMS (nm) to about 800 RMS (nm), remove from about 0.01 μm to about 20 μm of depth of the glass-ceramic article and reduce the initial gloss value to a reduced gloss value from about 10% to 30% at 60°, wherein the chemical etching solution is formed by mixing hydrofluoric acid and an ammonium fluoride salt, the concentration of hydrofluoric acid is from 1% to 6% by weight of the etching solution and the ammonium fluoride salt is 5% to 30% by weight of the etching solution; and
c) removing the chemical etching solution from the roughened surface.

17. A method of modifying a non-damaged surface of a glass-ceramic article having a major crystalline phase, the method comprising:
a) providing a glass-ceramic article having a non-damaged surface and an initial gloss value;
b) applying a chemical etching solution to the non-damaged surface of the glass-ceramic article for an etching time of about 5 s to less than 15 min to form a roughened surface having a target roughness value, remove from about 0.01 μm to about 20 μm of depth of the glass-ceramic article and reduce the initial gloss value to a reduced gloss value, wherein the chemical etching solution comprises hydrofluoric acid and an inorganic fluoride salt, the concentration of hydrofluoric acid is from 1% to 6% by weight of the etching solution and the inorganic fluoride salt is 5% to 30% by weight of the etching solution; and
c) removing the chemical etching solution from the roughened surface.

18. The method of claim 17 , wherein: the chemical etching solution further comprises from about 0.05 M to about 6 M of a mineral acid; and the reduced gloss value is from about 0.1% to about 30% at 60°; the target roughness value is from about 10 RMS (nm) to about 800 RMS (nm).

Assignees

• Corning Inc

Inventors

• Hou Jun
• Jin Yuhui
• Zhang Lu

Classifications

• C03C10/0018

  containing SiO2, Al2O3 and monovalent metal oxide as main constituents · CPC title

• C03C15/00 Primary

  Surface treatment of glass, not in the form of fibres or filaments, by etching (etching or surface-brightening compositions, in general C09K13/00) · CPC title

• C09K13/04 Primary

  containing an inorganic acid · CPC title

• B44C1/227

  by etching · CPC title

• G02F1/133502

  Antiglare, refractive index matching layers · CPC title