Modified thermoplastic polyurethane rolling film and preparation method

Patent metadata

Field	Value
Publication number	US-10035891-B2
Application number	US-201415113813-A
Country	US
Kind code	B2
Filing date	Dec 24, 2014
Priority date	Jan 24, 2014
Publication date	Jul 31, 2018
Grant date	Jul 31, 2018

Abstract

This present invention discloses a modified thermoplastic polyurethane (TPU) rolling film and relates to a preparation method thereof. The modified thermoplastic polyurethane (TPU) rolling film comprises: 100 parts by weight of TPU resin, 3 to 8 parts by weight of Thermoplastic polyolefin (TPO) resin, 5 to 10 parts by weight of Thermo Plastic Silicone Vulcanizate (TPSiV) resin, 5 to 15 parts by weight of TPU color masterbatch, 0.5 to 1.5 parts by weight of antioxidant, 0.5 to 1.5 parts by weight of light stabilizer, 10 to 15 parts by weight of flame retardant, and 0.03 to 0.1 parts by weight of compound lubricant. This kind of rolling film has a uniform thickness and high surface gloss, and is yellowing resistant, abrasion resistant, flame retardant, and low-temperature resistant.

First claim

What is claimed is:

1. A modified thermoplastic polyurethane (TPU) rolling film comprising:
100 parts by weight of TPU resin,
3 to 8 parts by weight of Thermoplastic polyolefin (TPO) resin,
5 to 10 parts by weight of Thermo Plastic Silicone Vulcanizate (TPSiV) resin,
5 to 15 parts by weight of TPU color masterbatch,
0.5 to 1.5 parts by weight of antioxidant,
0.5 to 1.5 parts by weight of light stabilizer,
10 to 15 parts by weight of flame retardant,
and 0.03 to 0.1 parts by weight of compound lubricant.

2. The composition as claimed in claim 1 wherein the TPU color masterbatch is prepared through an extruding and granulation process by mixing TPU resin with toner together.

3. The composition as claimed in claim 1 wherein the antioxidant is prepared by mixing β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid octadecanol ester with N, N′-hexamethylene bis (3,5-di-tert-butyl-4-hydroxyphenyl propionamide) at a mass ratio of 1:1.5.

4. The composition as claimed in claim 1 wherein the light stabilizer is prepared by mixing 2-(2′-hydroxy-3′,5′-cumylphenyl) benzotriazole with 2-(2′-hydroxy-3′,5′-di-tert-amyl-phenyl) benzotriazole at a mass ratio of 1:2.

5. The composition as claimed in claim 1 wherein the flame retardant is prepared by mixing organophosphate flame retardant with talcum powder of 5000 mesh at a mass ratio of 3:1.

6. The composition as claimed in claim 1 wherein the compound lubricant is prepared by mixing Erucamide with Oleic acid amide and Stearic acid at a mass ratio of 1:1:1.

7. A process of preparing a modified TPU rolling film as claimed in claim 1 comprising the following steps:
Step 1: add all ingredients according to the compositions specified in claims 1 - 6 to a stirring pot and stir the mixture evenly at a high speed under a temperature between 85° C. and 100° C.;
Step 2: pour the mixture from Step 1 into an internal mixer wherein the mixture is mixed for 3 to 5 minutes;
Step 3: the mixture from Step 2 is subsequently plasticated, extruded, and calendered using a rolling turbine, an extruder, and a calender, respectively.

8. The process according to claim 7 wherein the temperatures for plasticating, extruding, and calendaring as described in Step 3 are maintained at 130° C. to 150° C., 130° C. to 150° C., 140° C. to 160° C. respectively.

9. The process according to claim 7 wherein the TPU color masterbatch is prepared through an extruding and granulation process by mixing TPU resin with toner together.

10. The process according to claim 7 wherein the antioxidant is prepared by mixing β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid octadecanol ester with N, N′-hexamethylene bis (3,5-di-tert-butyl-4-hydroxyphenyl propionamide) at a mass ratio of 1:1.5.

11. The process according to claim 7 wherein the light stabilizer is prepared by mixing 2-(2′-hydroxy-3′,5′-cumylphenyl) benzotriazole with 2-(2′-hydroxy-3′,5′-di-tert-amyl-phenyl) benzotriazole at a mass ratio of 1:2.

12. The process according to claim 7 wherein the flame retardant is prepared by mixing organophosphate flame retardant with talcum powder of 5000 mesh at a mass ratio of 3:1.

13. The process according to claim 7 wherein the compound lubricant is prepared by mixing Erucamide with Oleic acid amide and Stearic acid at a mass ratio of 1:1:1.

Assignees

• Univ Fuzhou

Inventors

• Zheng Yuying
• Lin Jinxian

Classifications

• B29B7/005

  for mixing in batches · CPC title

• B29B7/02

  non-continuous, with mechanical mixing or kneading devices, i.e. batch type · CPC title

• B29C47/0021

  Operations & Transport · mapped topic

• B29K2083/00

  Use of polymers having silicon, with or without sulfur, nitrogen, oxygen, or carbon only, in the main chain, as moulding material · CPC title

• B29B9/12

  characterised by structure or composition · CPC title