Abstract

A glass laminate comprises an external glass sheet, an internal glass sheet, and a polymer interlayer formed between the external glass sheet and the internal glass sheet. The external glass sheet can be a thin chemically-strengthened glass sheet or can be a non-chemically strengthened glass sheet, the polymer interlayer can have a thickness of less than 1.6 mm, and the internal glass sheet can be a non-chemically-strengthened glass sheet or a thin chemically strengthened glass sheet.

First claim

What is claimed is:

1. An automotive laminate comprising:
an interior surface;
a non-chemically strengthened external glass sheet;
a chemically strengthened internal glass sheet; and
at least one polymer interlayer intermediate the external and internal glass sheets and comprising any one or more of polyvinyl butyral (PVB), polycarbonate, acoustic PVB, ethylene vinyl acetate (EVA), thermoplastic polyurethane (TPU), and ionomer,
wherein the internal glass sheet has a thickness of 1.0 mm or less,
wherein the external glass sheet has a thickness ranging from about 1.5 mm to about 3.0 mm,
wherein the internal glass sheet comprises an alkali aluminosilicate glass,
wherein the internal glass sheet includes one or more alkaline earth metal oxides, such that a content of alkaline earth metal oxides is at least 5 wt. %, and
wherein a surface of the internal glass sheet constitutes the interior surface of the automotive laminate.

2. The automotive laminate of claim 1 , wherein the internal glass sheet includes at least about 6 wt. % aluminum oxide.

3. The automotive laminate of claim 1 , wherein the internal glass sheet has a thickness of less than about 0.7 mm.

4. The automotive laminate of claim 1 , wherein the polymer interlayer comprises a single polymer sheet, a multilayer polymer sheet, or a composite polymer sheet.

5. The automotive laminate of claim 1 , wherein the polymer interlayer has a thickness of between about 0.4 to about 1.2 mm.

6. The automotive laminate of claim 1 , wherein the external glass sheet is a soda lime glass or an annealed glass.

7. The automotive laminate of claim 1 , wherein the external glass sheet has a thickness of about 2.1 mm.

8. The automotive laminate of claim 1 , wherein the glass laminate has an area greater than 1 m 2 .

9. The automotive laminate of claim 1 , wherein the laminate is an automotive windshield, sunroof or cover plate.

10. The automotive laminate of claim 1 , wherein the internal glass layer has a surface compressive stress between about 250 MPa and about 900 MPa.

11. The automotive laminate of claim 1 , wherein the internal glass layer has a surface compressive stress of between about 250 MPa and about 350 MPa and a DOL of compressive stress greater than about 20 μm.

12. The automotive laminate of claim 1 wherein a surface of the external glass sheet adjacent the interlayer is acid etched.

13. The automotive laminate of claim 1 wherein a surface of the internal glass sheet opposite the interlayer is acid etched.

14. An automotive laminate comprising:
an interior surface;
a non-chemically strengthened external glass sheet;
a chemically strengthened internal glass sheet; and
at least one polymer interlayer intermediate the external and internal glass sheets,
wherein the internal glass sheet comprises an alkali aluminosilicate glass and has a surface compressive stress between about 250 MPa and about 900 MPa,
wherein the internal glass sheet includes one or more alkaline earth metal oxides, such that a content of alkaline earth metal oxides is at least 5 wt. %,
wherein the external glass sheet comprises soda lime glass, and
wherein the interior surface consists of a surface of the internal glass sheet.

15. The automotive laminate of claim 14 , wherein the internal glass sheet has a surface compressive stress of between about 250 MPa and about 350 MPa and a DOL of compressive stress greater than about 20 μm.

16. The automotive laminate of claim 14 , wherein the internal glass sheet has a thickness ranging from about 0.5 mm to about 1.5 mm, and
wherein the external glass sheet has a thickness ranging from about 1.5 mm to about 3.0 mm.

17. The automotive laminate of claim 14 , wherein the polymer interlayer comprises a material selected from the group consisting of polyvinyl butyral (PVB), polycarbonate, acoustic PVB, ethylene vinyl acetate (EVA), thermoplastic polyurethane (TPU), ionomer, a thermoplastic material, and combinations thereof.

18. The automotive laminate of claim 14 , wherein the polymer interlayer has a thickness of between about 0.4 to about 1.2 mm.

19. An automotive laminate comprising:
an interior surface;
a non-chemically strengthened external glass sheet comprising a soda lime glass;
a chemically strengthened internal glass sheet comprising an alkali aluminosilicate glass and a surface compressive stress between about 250 MPa and about 900 MPa; and
at least one polymer interlayer intermediate the external and internal glass sheets and comprising any one or more of polyvinyl butyral (PVB), polycarbonate, acoustic PVB, ethylene vinyl acetate (EVA), thermoplastic polyurethane (TPU), and ionomer,
wherein the internal glass sheet has a thickness of 1 mm or less,
wherein the external glass sheet has a thickness ranging from about 1.5 mm to about 3.0 mm,
wherein a surface of the internal glass sheet constitutes the interior surface of the automotive laminate,
wherein the internal glass sheet includes one or more alkaline earth metal oxides, such that a content of alkaline earth metal oxides is at least 5 wt. %.

Assignees

• Corning Inc

Inventors

• Cleary Thomas Michael
• Huten Timothy Scott
• Moore Michael John

Classifications

• B32B17/10761

  containing vinyl acetal · CPC title

• B32B17/10137

  Chemical strengthening · CPC title

• B32B17/10036

  comprising two outer glass sheets · CPC title

• B32B17/10119

  having a composition deviating from the basic composition of soda-lime glass, e.g. borosilicate · CPC title

• Y10T428/24967

  Absolute thicknesses specified · CPC title