Ambient temperature curable isocyanate-free compositions for preparing crosslinked polyurethanes

Patent metadata

Field	Value
Publication number	US-10030104-B2
Application number	US-201615068823-A
Country	US
Kind code	B2
Filing date	Mar 14, 2016
Priority date	Mar 31, 2015
Publication date	Jul 24, 2018
Grant date	Jul 24, 2018

Abstract

The present invention provides a multicomponent composition that is substantially isocyanate-free and comprises a polycarbamate as a first component having a filler, pigment, extender or matting agent and a second component containing an acidic catalyst an alkanol having one OH group, a polyaldehyde and an acetal or hemiacetal of the polyaldehyde. The compositions are shelf stable and useful as two components and avoid problems caused by combining the catalyst with any filler, pigment, extender or matting agent.

First claim

We claim:

1. A substantially isocyanate-free two-component composition having a pH of 7.0 or less comprising:
as a first component,
one or more polycarbamate having two or more carbamate groups, and
one or more polymeric matting agent, filler, extender, or pigment in the amount of from 1 to 80 wt. %, based on the total solids of the first component, and,

as a second component,
from 5 to 90 wt. %, based on the total weight of the second component, of one or more alkanol having one OH group,
one or more polyaldehyde that has two or more aldehyde groups, or
one or more acetal or hemiacetal of the polyaldehyde, and
from 0.01 to 10 wt. % of one or more catalyst having a pK a of less than 5.0, based on the total weight of solids in the composition,

said composition having less than 5 mol % of isocyanate (—N═C═O) groups based on total moles of carbamate groups plus isocyanate groups in the composition;
wherein the first and second components when combined form a composition that reacts to cure at a temperature of from 0° C. to less than 80° C. to form a crosslinked polyurethane.

2. The two-component composition as claimed in claim 1 , wherein the alkanol having one OH group is a primary alcohol.

3. The two-component composition as claimed in claim 1 , wherein the catalyst is an organic or inorganic protic acid or salt thereof.

4. The two-component composition as claimed in claim 1 , wherein the catalyst is a sulfonic acid.

5. The two-component composition as claimed in claim 1 , wherein in the first component of the composition, the polycarbamate is the condensation product of one or more polyols with an unsubstituted carbamic acid alkyl ester or urea.

6. The two-component composition as claimed in claim 5 , wherein the one or more polyols is an acrylic polyol, or an alkyd polyol.

7. The two-component composition as claimed in claim 1 , wherein in the second component of the composition, the polyaldehyde from which the acetal or hemiacetal is formed preferably has a solubility in water of less than 0.15 gram of polyaldehyde per milliliter of water at 25° C.

8. The two-component composition as claimed in claim 1 , wherein the polyaldehyde in the second component is chosen from (cis,trans)-1,4-cyclohexane dicarboxyaldehydes, (cis,trans)-1,3-cyclohexanedicarboxyaldehydes and mixtures thereof.

9. The two-component composition as claimed in claim 1 , comprising one or more pigments, fillers or extenders chosen from any metal oxides, metal carbonates, silica, and alkali metal silicates.

10. The two-component composition as claimed in claim 1 , wherein the blend ratio of the first component to the second component from is from 2:1 to 5:1 by weight.

11. The two-component composition as claimed in claim 1 , wherein the one or more polyaldehyde is a dialdehyde.

12. The two-component composition as claimed in claim 1 , wherein the one or more polyaldehyde is a cyclic dialdehyde.

13. The two-component composition as claimed in claim 1 , wherein the one or more polyaldehyde is a cycloaliphatic dialdehyde.

Assignees

• Dow Global Technologies Llc

Inventors

• Argyropoulos John N
• Anderson Jeff R
• Kamber Nahrain E
• Ortiz Rebecca S

Classifications

• C08G71/04 Primary

  Polyurethanes · CPC title

• C09D175/04

  Polyurethanes · CPC title

• C08G12/46

  Block or graft polymers prepared by polycondensation of aldehydes or ketones on to macromolecular compounds · CPC title

• C09D175/12

  from compounds containing nitrogen and active hydrogen, the nitrogen atom not being part of an isocyanate group · CPC title