Machining methods of forming laminated glass structures

Patent metadata

Field	Value
Publication number	US-10029941-B2
Application number	US-201515300118-A
Country	US
Kind code	B2
Filing date	Mar 26, 2015
Priority date	Mar 31, 2014
Publication date	Jul 24, 2018
Grant date	Jul 24, 2018

Abstract

A method of shaping a laminated glass structure includes providing the laminated glass structure comprising a flexible glass sheet having a thickness of no greater than about 0.3 mm laminated to a non-glass substrate by an adhesive layer. The flexible glass structure and adhesive layer are ground using a first tool to remove glass material. The non-glass substrate is cut with a second tool different from the first tool through a kerf formed through the flexible glass structure thereby forming a shaped laminated glass structure. A glass edge strength of a cut edge of the shaped laminated glass structure is at least about 20 MPa.

First claim

What is claimed is:

1. A method of shaping a laminated glass structure comprising a flexible glass sheet having a thickness of no greater than about 0.3 mm laminated to a non-glass substrate by an adhesive layer, the method comprising:
cutting the flexible glass structure and adhesive layer using a first tool to remove glass material; and
cutting the non-glass substrate with a second tool different from the first tool through a kerf formed through the flexible glass structure thereby forming a shaped laminated glass structure;
wherein a glass edge strength of a cut edge of the shaped laminated glass structure is at least about 20 MPa.

2. The method of claim 1 , wherein the first tool is an abrasive wheel having an ISO/FEPA grit designation of at least 180.

3. The method of claim 1 , wherein the second tool is a metal wire electrode of a wire-cut EDM machine.

4. The method of claim 1 , wherein the first tool is a first abrasive wheel and the second tool is a second abrasive wheel having an ISO/FEPA grit designation different from the first abrasive wheel.

5. The method of claim 4 , wherein the step of cutting the flexible glass structure and adhesive layer using the first tool comprises grinding the flexible glass structure using the first abrasive wheel to form the kerf.

6. The method of claim 5 , wherein the second abrasive wheel has a width less than a width of the kerf.

7. The method of claim 1 , wherein the first tool is an abrasive wheel and the second tool is a metal wire electrode of a wire-cut EDM machine.

8. The method of claim 7 , wherein the step of cutting the flexible glass structure and adhesive layer using the first tool comprises grinding the flexible glass structure using the abrasive wheel to form the kerf.

9. The method of claim 8 , wherein the metal wire electrode has a diameter less than a width of the kerf.

10. The method of claim 1 , wherein the first tool is a first region of an abrasive wheel having a first ISO/FEPA grit designation and the second tool is a second region of the abrasive wheel having a second ISO/FEPA grit designation different from the first ISO/FEPA grit designation.

11. A method of shaping a laminated glass structure comprising a flexible glass sheet having a thickness of no greater than about 0.3 mm laminated to a non-glass substrate by an adhesive material;
supporting the preform laminated glass structure on a support surface such that the non-glass substrate is located between the flexible glass sheet and the support surface; and
cutting the non-glass substrate with a tool through a kerf formed through the flexible glass structure thereby forming a shaped laminated glass structure.

12. The method of claim 11 , wherein a glass edge strength of a cut edge of the shaped laminated glass structure at least about 20 MPa.

13. The method of claim 11 , wherein the tool is an abrasive wheel having an ISO/FEPA grit designation of at least 180.

14. The method of claim 11 , wherein the tool is a first tool, the method further comprising cutting the flexible glass structure and adhesive layer using a second tool forming the kerf.

15. The method of claim 14 , wherein second tool is a metal wire electrode of a wire-cut EDM machine.

16. The method of claim 14 , wherein the first tool is a first abrasive wheel and the second tool is a second abrasive wheel having an ISO/FEPA grit designation different from the first abrasive wheel.

17. The method of claim 16 , wherein the first abrasive wheel has a width less than a width of the kerf.

18. The method of claim 14 , wherein the first tool is a metal wire electrode of a wire-cut EDM machine and the second tool is an abrasive wheel.

19. The method of claim 18 , wherein the metal wire electrode has a diameter less than a width of the kerf.

20. The method of claim 14 , wherein the first tool is a first region of an abrasive wheel having a first ISO/FEPA grit designation and the second tool is a second region of the abrasive wheel having a second ISO/FEPA grit designation different from the first ISO/FEPA grit designation.

Assignees

• Corning Inc

Inventors

• Forenz Dominick John
• Mckendrick Walter Jay
• Price Michael William

Classifications

• B24B27/0675

  methods therefor · CPC title

• B24B27/0608

  using a saw movable on slideways · CPC title

• C03B33/078

  Polymeric interlayers · CPC title

• C03B33/10 Primary

  Glass-cutting tools, e.g. scoring tools · CPC title

• C03B33/02

  Cutting or splitting sheet glass {or ribbons}; Apparatus or machines therefor (C03B33/09 takes precedence; glass-cutting tools C03B33/10) · CPC title