Method of forming layered coating film

Patent metadata

Field	Value
Publication number	US-10022749-B2
Application number	US-201615065692-A
Country	US
Kind code	B2
Filing date	Mar 9, 2016
Priority date	Mar 31, 2015
Publication date	Jul 17, 2018
Grant date	Jul 17, 2018

Abstract

A method of forming a layered coating film includes: coating a workpiece with an electrodeposition coating material to form an electrodeposition coating layer; applying a colored coating material including a white pigment over the electrodeposition coating layer to form two or more colored coating layers that are layered on the electrodeposition layer; and applying a clear coating material over the two or more colored coating layers. The colored coating material includes coating materials respectively applied to form a lower-side colored coating layer and an upper-side colored coating layer of the two or more colored coating layers. A concentration of the white pigment in the coating material applied to form the lower-side colored coating layer is equal to or higher than a concentration of the white pigment included in the coating material applied to form the upper-side colored coating layer.

First claim

The invention claimed is:

1. A method of forming a layered coating film, the method comprising:
coating a workpiece with an electrodeposition coating material to form an electrodeposition coating layer;
applying a colored coating material over the electrodeposition coating layer to form two or more colored coating layers that are layered on the electrodeposition layer, the applying of the colored coating material including:
applying a first coating material that includes a white pigment comprising zinc oxide, a brilliant pigment and a first coloration pigment to form a lower-side colored coating layer; and
applying a second coating material that does not include a white pigment and includes a second coloration pigment, to form an upper-side colored coating layer onto a surface of the lower-side colored coating layer; and

applying a clear coating material onto a surface of the upper-side colored coating layer,
wherein the applying of the colored coating material further comprises:
after the applying of the first coating material, performing a first heat treatment to cure the first coating material; and
after the applying of the second coating material, performing a second heat treatment to cure the second coating material.

2. The method of forming the layered coating film according to claim 1 , wherein the colored coating material further includes a resin and a pigment, and
an amount of the white pigment added to the colored coating material is equal to or larger than 2.5 mass % based on a total amount of the resin and the pigment.

3. The method of forming the layered coating film according to claim 1 , wherein the two or more colored coating layers comprise two colored coating layers that are the lower-side colored coating layer and the upper-side colored coating layer.

4. The method of forming the layered coating film according to claim 2 , wherein the two or more colored coating layers comprise two colored coating layers that are the lower-side colored coating layer and the upper-side colored coating layer.

5. The method of forming the layered coating film according to claim 1 , wherein the applying of the colored coating material further includes:
mixing and stirring the white pigment with a resin and a pigment to form the first coating material.

6. The method of forming the layered coating film according to claim 5 , wherein the applying of the colored coating material further includes:
after the mixing and stirring of the white pigment with the resin and the pigment, adding water to the first coating material in an amount ranging from 150 parts by mass to 300 parts by mass.

7. The method of forming the layered coating film according to claim 1 , wherein the first and second heat treatments comprise heating the coating material in a range from 100° C. to 170° C. for a duration in a range from 10 minutes to 40 minutes.

8. The method of forming the layered coating film according to claim 1 , wherein a thickness of each of the lower-side colored coating layer and the upper-side colored coating layer is in a range from 5 μm to 15 μm.

9. The method of forming the layered coating film according to claim 1 , wherein the brilliant pigment comprises at least one of an aluminum pigment and an interference mica pigment.

10. The method of forming the layered coating film according to claim 1 , wherein the brilliant pigment comprises at least one of an aluminum pigment and an interference mica pigment, the first coloration pigment comprises at least one of a phthalocyanine pigment and a dioxazine pigment, and the second coloration pigment comprises at least one of a phthalocyanine pigment and a dioxazine pigment.

11. The method of forming the layered coating film according to claim 2 , wherein the resin comprises a water-based thermosetting coating resin including one of an acrylic resin, a polyester resin, an epoxy resin, a polyurethane resin, and a polyurethane-acrylic resin.

12. The method of forming the layered coating film according to claim 11 , wherein the resin comprises a crosslinking agent including one of a melamine resin, and a blocked isocyanate.

13. A method of forming a layered coating film, the method comprising:
coating a workpiece with an electrodeposition coating material to form an electrodeposition coating layer;
applying a first coating material to form a lower-side colored coating layer on a surface of the electrodeposition coating layer;
applying a second coating material to form an upper-side colored coating layer on a surface of the lower-side colored coating layer; and
applying a clear coating material onto a surface of the upper-side colored coating layer,
wherein the first coating material includes a first composite pigment that consists of, by mass ratio of solid content, 4.74 to 5.08 of aluminum pigment, 2.1 to 8.7 of zinc oxide, 10.15 to 10.89 of phthalocyanine pigment, 0.67 to 0.72 of dioxazine pigment, 0.01 of carbon black and 6.43 to 6.72 of barium sulphate, and
wherein the second coating material includes a second composite pigment that consists of, by mass ratio of solid content, 0 to 8.5 of zinc oxide, 1.04 to 1.12 of phthalocyanine pigment, 0.01 of dioxazine pigment, 0.01 of carbon black and 6.64 to 7.16 of barium sulphate.

14. The method of forming the layered coating film according to claim 1 , wherein in the applying of the first coating material, the first coating material is applied onto a surface of the electrodeposition coating layer.

15. A method of forming a layered coating film, the method comprising:
coating a workpiece with an electrodeposition coating material to form an electrodeposition coating layer;
forming a first colored coating layer, comprising:
mixing and stirring white pigment comprising zinc oxide with a resin and a pigment to form a first coating material;
applying the first coating material onto the coated workpiece; and
performing a heat treatment of the first coating material;

forming a second colored coating layer, comprising:
mixing and stirring a resin and a pigment to form a second coating material, the second coating material not including a white pigment;
applying the second coating material onto the first colored coating layer; and
performing a heat treatment of the second coating material; and

applying a clear coating material onto the second colored coating layer,
wherein an amount of the white pigment in the first coating material is equal to or greater than 2.5 mass % based on a total amount of the resin and the pigment in the first and second coating materials.

Assignees

• Fuji Heavy Ind Ltd
• Subaru Corp

Inventors

• Ishizaka Junichi
• Nakamura Takeshi
• Tsukakoshi Tsuneo

Classifications

• C25D5/48

  After-treatment of electroplated surfaces · CPC title

• B05D1/04

  involving the use of an electrostatic field {(B05D1/025 and B05D1/14 take precedence)} · CPC title

• B05D7/577

  some layers being coated "wet-on-wet", the others not · CPC title

• B05D7/57 Primary

  the last layer being a clear coat · CPC title

• B05D2601/02

  used for pigmentation effect, e.g. metallic effect · CPC title