Strontium magnesium molybdenum oxide material having double perovskite structure and method for preparing the same

Patent metadata

Field	Value
Publication number	US-10020515-B2
Application number	US-201615209928-A
Country	US
Kind code	B2
Filing date	Jul 14, 2016
Priority date	Jul 14, 2016
Publication date	Jul 10, 2018
Grant date	Jul 10, 2018

Abstract

The present invention relates to a strontium magnesium molybdenum oxide material having perovskite structure and the method for preparing the same. Citric acid is adopted as the chelating agent. By using sol-gel pyrolysis and replacing a portion of strontium in Sr 2 MgMoO 6-δ by cerium and a portion of magnesium by copper, a material with a chemical formula of Sr 2-x Ce x Mg 1-y Cu y MoO 6-δ is produced, where 0≤x<2, 0<y<1, and 0<δ<6. Thereby, the electrical conductivity of the material is improved. The perovskite-type cerium- and copper-replaced strontium magnesium molybdenum oxide significantly increases the electrical conductivity of the material and can be applied as the anode material for solid oxide fuel cell (SOFC).

First claim

What is claimed is:

1. A perovskite-type strontium magnesium molybdenum oxide material, having a chemical formula of Sr 2-x Ce x Mg 1-y Cu y MoO 6-δ , where 0≤x<2, 0<y<1, and 0<δ<6.

2. A method for preparing a perovskite-type strontium magnesium molybdenum oxide material, comprising steps of:
mixing and dissolving strontium nitrate powder, magnesium nitrate hexahydrate powder, ammonium molybdate hexahydrate powder, copper nitrate powder, and cerium nitrate powder in deionized water to form a mixed solution;
adding citric acid to said mixed solution to form a gel;
baking said gel to form precursor powder; and
calcining said precursor powder to form a perovskite-type strontium magnesium molybdenum oxide material with a chemical formula of Sr 2-x Ce x Mg 1-y Cu y MoO 6-δ , where 0≤x<2, 0<y<1, and 0<δ<6;

where the molar ratios of said strontium nitrate powder, said magnesium nitrate hexahydrate powder, said ammonium molybdate hexahydrate powder, said copper nitrate powder, and said cerium nitrate powder correspond to the molar ratios of the composing elements in said chemical formula.

3. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , wherein said step of forming said mixed solution is performed at the temperature of 50-70° C.

4. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , wherein said step of forming said gel is performed at the temperature of 70-90° C.

5. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , wherein the molar ratio of said citric acid to the metal ions in said mixed solution is 1:1.

6. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , wherein said step of forming said precursor powder is to bake said gel at 100-120° C.

7. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , and before said step of calcining said precursor powder, further comprising a step of performing thermal treatments on said precursor powder in two stages to decompose the organics in said precursor powder; the temperature of one stage of said thermal treatment being 300-500° C.; and the temperature of the other stage of said thermal treatment being 700-1000° C.

8. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 2 , wherein said step of calcining said precursor powder is to first calcine in atmosphere for 8-24 hours and then calcine in hydrogen reduction ambient for 20-48 hours.

9. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 8 , wherein the calcining temperature is 1200° C.-1300° C. in atmosphere.

10. The method for preparing a perovskite-type strontium magnesium molybdenum oxide material of claim 8 , wherein the reduction temperature is 800° C. in hydrogen ambient.

Assignees

• Iner Aec Executive Yuan

Inventors

• Chung Tsui-Yun
• Liu Chien-Kuo
• Lin Jing-Kai
• Tseng Hui-Ping
• Lee Ruey-Yi

Classifications

• C04B2235/664

  Reductive annealing · CPC title

• C04B2235/3206

  Magnesium oxides or oxide-forming salts thereof · CPC title

• C04B35/62675

  characterised by the treatment temperature · CPC title

• C04B2235/443

  Nitrates or nitrites · CPC title

• C04B2235/3256

  Molybdenum oxides, molybdates or oxide forming salts thereof, e.g. cadmium molybdate · CPC title