Corona-resistant resin composition, method for developing corona resistance of resin composition, and corona-resistant member

Patent metadata

Field	Value
Publication number	US-10017643-B2
Application number	US-201415029697-A
Country	US
Kind code	B2
Filing date	Oct 24, 2014
Priority date	Oct 29, 2013
Publication date	Jul 10, 2018
Grant date	Jul 10, 2018

Abstract

A corona-resistant resin composition and a corona-resistant member, having sufficient durability relative to corona discharge, are provided. A corona-resistant resin composition obtained, at least, by melt kneading 7 to 80 parts by mass of a silicone-based polymer per 100 parts by mass of a resin component, and a corona-resistant member formed by molding the corona-resistant resin composition, are disclosed. A polyarylene sulfide resin or a polybutylene terephthalate resin may be used as the resin component.

First claim

The invention claimed is:

1. A corona-resistant resin composition obtained by, at least, melt kneading a mixture including a resin component and 7 to 80 parts by mass of at least one silicone-based polymer selected from the group consisting of a silicone-acrylic core-shell rubber and a silicone-acrylic copolymer per 100 parts by mass of the resin component, the resin component being a polyarylene sulfide resin.

2. The corona-resistant resin composition according to claim 1 , wherein the mixture further includes glass fiber.

3. A corona-resistant member formed by molding the corona-resistant resin composition according to claim 1 .

4. The corona-resistant member according to claim 3 , wherein, when the corona-resistant member is inspected using a scanning electron microscope, the corona-resistant member shows that domains of the silicone-based polymer are interspersed within a matrix of the resin component, and an average dispersed diameter of the silicone-based polymer within the matrix of the resin component, when measured using an image captured using the scanning electron microscope, is at least 0.1 μm but not more than 20 μm.

5. The corona-resistant member according to claim 3 , wherein the corona resistant member has a sheet-like form, a plate-like form, a cylindrical form, or a coating-like form.

6. The corona-resistant resin composition according to claim 1 , wherein the silicone-based polymer includes a silicone-acrylic copolymer.

7. The corona-resistant resin composition according to claim 1 , wherein the amount of the silicone-based polymer is 30 to 80 parts by mass per 100 parts by mass of the resin component.

8. The corona-resistant resin composition according to claim 1 , wherein the silicon-based polymer includes a silicone-acrylic core-shell rubber.

9. A method for developing corona resistance of a resin composition, the method comprising adding 7 to 80 parts by mass of at least one silicone-based polymer selected from the group consisting of a silicone-acrylic core-shell rubber and a silicone-acrylic copolymer per 100 parts by mass of a resin component in a resin composition, thereby developing corona resistance, the resin component being a polyarylene sulfide resin.

10. The method according to claim 9 , wherein the silicone-based polymer includes a silicone-acrylic copolymer.

11. The method according to claim 9 , wherein the amount of the silicone-based polymer is 30 to 80 parts by mass per 100 parts by mass of the resin component.

12. The method according to claim 9 , further comprising adding a grass fiber in the resin composition.

13. The method according to claim 9 , wherein the silicone-based polymer includes a silicone-acrylic core-shell rubber.

Assignees

• Polyplastics Co

Inventors

• Arai Hiroki

Classifications

• C09D181/04

  Polysulfides · CPC title

• C08L81/04 Primary

  Polysulfides · CPC title

• C08L51/085

  on to polysiloxanes · CPC title

• C08L67/02 Primary

  Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence) · CPC title

• C08K7/14

  Glass · CPC title