Method and apparatus for manufacturing foamed resin metal laminated sheet

Patent metadata

Field	Value
Publication number	US-10016965-B2
Application number	US-201314419123-A
Country	US
Kind code	B2
Filing date	Aug 21, 2013
Priority date	Aug 24, 2012
Publication date	Jul 10, 2018
Grant date	Jul 10, 2018

Abstract

When a foamed resin metal laminated sheet ( 1 ) heated in a heating furnace ( 11 ) is cooled to room temperature, the foamed resin metal laminated sheet ( 1 ) is held at soaking temperature in a soaking bath ( 21 ) to make the temperature of the foamed resin sheet uniform over the entire area of the foamed resin metal laminated sheet ( 1 ), and then cooled to room temperature in a room temperature cooling unit ( 22 ). Thus, rippling due to thermal strain can be suppressed.

First claim

The invention claimed is:

1. A method for manufacturing a foamed resin metal laminated sheet, comprising the steps of:
laminating a first metal plate on one side and a second metal plate on the other side of a foamable resin sheet in an unfoamed state to form a foamable resin metal laminated sheet;
heating the foamable resin metal laminated sheet and foaming the foamable resin sheet to form a foamed resin metal laminated sheet; and
cooling the foamed resin metal laminated sheet to room temperature, the cooling step comprising:
cooling the foamed resin metal laminated sheet to a soaking temperature lower than a foaming temperature of the foamable resin sheet and higher than the room temperature, and holding the foamed resin metal laminated sheet at the soaking temperature until a surface temperature of the middle area of each of the metal plates becomes equal to a surface temperature of a peripheral area of each of the metal plates, respectively; and
cooling the foamed resin metal laminated sheet to the room temperature after the step of cooling to the soaking temperature and holding at the soaking temperature, and

wherein the soaking temperature is set in the range of not lower than Tm but not higher than 1.3 Tm, where Tm represents a melting point of a foamed resin of the foamable resin sheet, such that the formed resin sheet is in a melted state in the entire area of the formed resin metal laminated sheet held at the soaking temperature.

2. The method for manufacturing the foamed resin metal laminated sheet according to claim 1 , wherein the cooling step further comprises, between the step of cooling to the soaking temperature and the step of cooling to the room temperature, a step of cooling the foamed resin metal laminated sheet at a second soaking temperature lower than the soaking temperature and higher than the room temperature, and holding the foamed resin metal laminated sheet at the second soaking temperature.

3. The method for manufacturing the foamed resin metal laminated sheet according to claim 2 , wherein the foamable resin sheet contains polypropylene and the metal plates contain aluminum.

4. The method for manufacturing the foamed resin metal laminated sheet according to claim 1 , wherein the foamable resin sheet contains polypropylene and the metal plates contain aluminum.

5. A method for manufacturing a foamed resin metal laminated sheet, comprising the steps of:
laminating a first metal plate on one side and a second metal plate on the other side of a foamable resin sheet in an unfoamed state to form a foamable resin metal laminated sheet;
heating the foamable resin metal laminated sheet and foaming the foamable resin sheet to form a foamed resin metal laminated sheet; and
cooling the foamed resin metal laminated sheet to room temperature, the cooling step comprising:
cooling the foamed resin metal laminated sheet by natural convection and radiation in air to a soaking temperature lower than a foaming temperature of the foamable resin sheet and higher than the room temperature, and holding the foamed resin metal laminated sheet at the soaking temperature until a surface temperature of the middle area of each of the metal plates becomes equal to a surface temperature of a peripheral area of each of the metal plates, respectively; and
cooling the foamed resin metal laminated sheet to the room temperature after the step of cooling to the soaking temperature and holding at the soaking temperature, and

wherein the soaking temperature is set in the range of not lower than Tm but not higher than 1.3 Tm, where Tm represents a melting point of a foamed resin of the foamable resin sheet, such that the formed resin sheet is in a melted state in the entire area of the formed resin metal laminated sheet held at the soaking temperature.

Assignees

• Kobe Steel Ltd

Inventors

• Sugimoto Akio

Classifications

• B32B37/0015

  to avoid warp or curl · CPC title

• B32B2266/025

  Polyolefin · CPC title

• B29C44/3484

  Stopping the foaming reaction until the material is heated or re-heated · CPC title

• B32B15/085

  comprising polyolefins · CPC title

• B29C35/16

  Cooling {(cooling extruded material B29C48/911; cooling preforms for blow moulding B29C49/6427; cooling blown articles B29C49/66; cooling tyres during post cure inflation B29D30/0643)} · CPC title