Polyurethane pultrusion formulations for the production of articles with improved coating adhesion and articles produced therefrom

Patent metadata

Field	Value
Publication number	US-10005877-B2
Application number	US-201414893350-A
Country	US
Kind code	B2
Filing date	Jun 18, 2014
Priority date	Jun 25, 2013
Publication date	Jun 26, 2018
Grant date	Jun 26, 2018

Abstract

Polyurethane composites to which paint will adhere without the need for an aggressive pretreatment are produced by a pultrusion process using a polyurethane-forming system that includes a polyisocyanate component containing at least one polyisocyanate and an isocyanate-reactive component containing at least one cashew oil-based polyether polyol.

First claim

What is claimed is:

1. A polyurethane-forming system suitable for the production of a fiber reinforced composite to which a coating may be applied with minimal pretreatment comprising:
a) a polyisocyanate component comprising at least one polyisocyanate, and
b) an isocyanate-reactive component comprising 20% to 30% by weight, based on total weight of the isocyanate-reactive component, of at least one cashew oil-based polyether polyol wherein the cashew oil-based polyol has a hydroxyl number of from 175 to 550 and a functionality of from 2 to 5.

2. The system of claim 1 in which the isocyanate-reactive component includes up to 40% by weight of a polyol having a number average molecular weight of at least 1500 Da.

3. The system of claim 1 in which the isocyanate-reactive component includes up to 40% by weight of a polyol having a number average molecular weight of less than 1500 Da.

4. The system of claim 1 in which the at least one cashew oil-based polyether polyol has a viscosity less than 4000 cps.

5. The system of claim 1 in which the isocyanate-reactive component has a hydroxyl number of between 400 and 420.

6. The system of claim 1 in which the isocyanate component and the isocyanate-reactive component are combined in amounts such that the isocyanate index is 70 to 150%.

7. The system of claim 1 , wherein the system further comprises an internal mold release agent.

8. A pultrusion process for preparing a fiber reinforced polyurethane composite with improved paint adhesion, the process comprising:
a) continuously pulling a roving or tow of continuous fiber reinforcing material successively through an impregnation chamber and a die;
b) continuously feeding a polyurethane-forming system comprising a polyisocyanate component comprising at least one polyisocyanate, and an isocyanate-reactive component comprising at least one cashew oil-based polyether polyol to the impregnation chamber, wherein the at least one cashew oil-based polyether polyol is present in an amount of 20% to 30% by weight, based on total weight of the isocyanate-reactive component, has a hydroxyl number of from 175 to 550 and a functionality of from 2 to 5;
c) contacting the fiber reinforcing material with the polyurethane-forming system in the impregnation chamber in a manner such that substantially complete wetting of the fiber reinforcing material by the polyurethane-forming system occurs;
d) directing the fiber reinforcing material from c) through a die heated to reaction temperature to form a solid composite; and
e) drawing the composite from the die.

9. The pultrusion process of claim 8 in which the fiber reinforcing material is selected from the group consisting of single strands, braided strands, woven mat structures, non-woven mat structures and combinations thereof.

10. The pultrusion process of claim 8 in which the fiber reinforcing material comprises one or more of glass fibers, glass mats, carbon fibers, polyester fibers, natural fibers, aramid fibers, basalt fibers and nylon fibers.

11. The pultrusion process of claim 8 in which the at least one cashew oil-based polyether polyol has a viscosity of less than 2000 cps.

12. The pultrusion process of claim 8 in which the isocyanate-reactive component has a hydroxyl number of from about 100 to about 1,000.

13. The pultrusion process of claim 8 , wherein the polyurethane-forming system further comprises an internal mold release agent.

14. A composite produced by the process of claim 8 .

15. A painted composite produced by applying paint to the composite of claim 14 .

16. A polyurethane composite comprising:
a) 30 to 95% by weight, based on the weight of the composite, of a fiber reinforcing material; and
b) a polyurethane that is a reaction product of a reaction mixture comprising:
i) a polyisocyanate component comprising at least one polyisocyanate, and
ii) an isocyanate-reactive component comprising 20% to 30% by weight, based on total weight of the isocyanate-reactive component, of at least one cashew oil-based polyether polyol, wherein the cashew oil-based polyol has a hydroxyl number of from 175 to 550 and a functionality of from 2 to 5.

17. The composite of claim 16 , further comprising an internal mold release agent.

Assignees

• Covestro Llc

Inventors

• Harasin Stephen J
• Hayes John E
• Sounik David

Classifications

• C08K7/14

  Glass · CPC title

• C08G18/4816

  mixtures of two or more polyetherpolyols having at least three hydroxy groups · CPC title

• C08G18/4891

  modified with higher fatty oils or their acids or by resin acids · CPC title

• C08G18/7664

  containing alkylene polyphenyl groups · CPC title

• B29K2075/00

  Use of {PU, i.e.} polyureas or polyurethanes {or derivatives thereof}, as moulding material · CPC title