Separator having binder layer, and electrochemical device comprising the separator and method of preparing the separator

Patent metadata

Field	Value
Publication number	US-10002719-B2
Application number	US-201514691085-A
Country	US
Kind code	B2
Filing date	Apr 20, 2015
Priority date	Apr 21, 2014
Publication date	Jun 19, 2018
Grant date	Jun 19, 2018

Abstract

The present disclosure provides a separator comprising a porous substrate, a porous coating layer and a binder layer, the binder comprising at least one homopolymer of polyvinylidene fluoride and at least one copolymer of polyvinylidene fluoride (PVDF)-co-hexafluoropropylene (HFP) so that a content difference of hexafluoropropylene (HFP) present in the two compounds is about 3 wt % or higher.

First claim

The invention claimed is:

1. A separator, comprising:
a porous substrate having multiple pores;
a porous coating layer formed on at least one surface of the porous substrate comprising a mixture of inorganic particles and a binder,
the binder comprising at least one compound of formula (I) and at least one compound of formula (II) so that a content difference between hexafluoropropylene (HFP) in the compound of formula (I) and that in the compound of formula (II) is 3 wt % or higher, wherein the binder is present in an amount of 3 to 50 parts by weight based on 100 parts by weight of the inorganic particles;
a binder layer comprising at least one compound of formula (I) and at least one compound of formula (II),
wherein a fraction of the compound of formula (II) in both of the porous coating layer and the binder layer is greater than 10% and less than 99%, the fraction being calculated by dividing the content of the compound of formula (II) with the total content of the compound of formula (I) and the compound of formula (II), and a fraction of the compound of formula (II) in the binder layer is 50% to 99%:
-(VDF) a -(HFP) b -  (I)

-(VDF) c -(HFP) d -  (II)

wherein, VDF represents vinylidene fluoride,
HFP represents hexafluoropropylene, and
each of a, b, c and d represents wt %, provided that a+b=100, c+d=100, b≥0, d>0 and d−b≥3.

2. The separator of claim 1 , wherein the fraction of the compound of formula (II) in both of the porous coating layer and the binder layer is 30% to 90%.

3. The separator of claim 1 , wherein the porous coating layer further comprises a dispersant.

4. The separator of claim 3 , wherein the dispersant is any one selected from acrylic copolymers and a mixture thereof.

5. The separator of claim 3 , wherein the dispersant is present in an amount of 0.5 to 5 parts by weight based on 100 parts by weight of the inorganic particles.

6. The separator of claim 4 , wherein the acrylic copolymers contain at least one functional group selected from the group consisting of OH, COOH, CN, amine, amide and a combination thereof.

7. The separator of claim 1 , wherein the porous substrate is a polymer membrane or a multiple-membrane thereof, a woven fabric or a non-woven fabric made of a polymer selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate, polybutylene terephthalate, polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone, polyaryl ether ketone, polyetherimide, polyamideimide, polybenzimidazole, polyethersulfone, polyphenyleneoxide, cyclic olefin copolymer, polyphenylenesulfide, polyethylene naphthalate and a mixture thereof.

8. The separator of claim 1 , wherein the inorganic particles are selected from the group consisting of inorganic particles having a dielectric constant of 5 or higher, inorganic particles capable of transporting lithium ions, and a mixture thereof.

9. An electrochemical device, a cathode, an anode, and the separator of claim 1 being interposed between the cathode and the anode.

10. The electrochemical device of claim 9 , which is a lithium secondary battery.

11. A method of preparing a separator, comprising:
dissolving a binder in a polar solvent to obtain a binder solution, the binder comprising at least one compound of formula (I) and at least one compound of formula (II) so that a content difference between hexafluoropropylene (HFP) in the compound of formula (I) and that in the compound of formula (II) is 3 wt % or higher;
adding inorganic particles to the binder solution, followed by stirring, to obtain a slurry containing the inorganic particles dispersed therein, wherein the binder is used in an amount of 3 to 50 parts by weight based on 100 parts by weight of the inorganic particles; and
coating the slurry on at least one surface of a porous substrate, followed by drying, to form a porous coating layer on at least one surface of the porous substrate or on at least one pore-bearing area in the porous substrate, the porous coating layer comprising a binder layer in the outermost part thereof in the thickness direction of the porous substrate, the binder layer having the compound of formula (II) in a fraction of 50% to 99%, the fraction being calculated by dividing the content of the compound of formula (II) with the total content of the compound of formula (I) and the compound of formula (II),
wherein a fraction of the compound of formula (II) in the binder solution is greater than 10% and less than 99%:
-(VDF) a -(HFP) b -  (I)

-(VDF) c -(HFP) d -  (II)

wherein, VDF represents vinylidene fluoride,
HFP represents hexafluoropropylene, and
each of a, b, c and d represents wt %, provided that a+b=100, c+d=100, b≥0, d>0 and d−b≥3.

12. The method of claim 11 , wherein the fraction of the compound of formula (II) in the binder solution is 30% to 90%.

13. The method of claim 11 , wherein the binder solution further comprises a dispersant.

14. The method of claim 13 , wherein the dispersant is any one selected from acrylic copolymers and a mixture thereof.

15. The method of claim 13 , wherein the dispersant is used in an amount of 0.5 to 5 parts by weight based on 100 parts by weight of the inorganic particles.

16. The method of claim 14 , wherein the acrylic copolymers contain at least one functional group selected from the group consisting of OH, COOH, CN, amine, amide and a combination thereof.

17. The method of claim 11 , wherein the porous substrate is a polymer membrane or a multiple-membrane thereof, a woven fabric or a non-woven fabric made of a polymer selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate, polybutylene terephthalate, polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone, polyaryl ether ketone, polyetherimide, polyamideimide, polybenzimidazole, polyethersulfone, polyphenyleneoxide, cyclic olefin copolymer, polyphenylenesulfide, polyethylene naphthalate and a mixture thereof.

18. The method of claim 11 , wherein the inorganic particles are selected from the group consisting of inorganic particles having a dielectric constant of 5 or higher, inorganic particles capable of transporting lithium ions, and a mixture thereof.

19. The method of claim 11 , wherein the polar solvent has a boiling point less than 100° C.

20. The method of claim 11 , wherein the polar solvent is selected from the group consisting of acetone, tetrahydrofuran, methylene chloride, chloroform, dimethylformamide, N-methyl-2-pyrrolidone (NMP), cyclohexane, water and a mixture thereof.

21. The method of claim 11 , wherein the polar solvent is used in an amount of 50 to 90 parts by weight based on 100 parts by weight of the total of the inorganic particles, the binder, the dispersant and the polar solvent.

22. The method of claim 11 , wherein the slurry is applied at a humidity of 10% or higher.

23. A separator prepared by the method of claim 11 .

Assignees

• Lg Chemical Ltd
• Toray Industries

Inventors

• Ha Jeong-Min
• Yoon Su-Jin
• Kim Jong-Hun
• Shin Byoung-Jin
• Lee Joo-Sung
• Kim Jin-Woo
• Han Da-Kyung

Classifications

• H01M50/457

  comprising three or more layers · CPC title

• H01M50/451

  comprising layers of only organic material and layers containing inorganic material · CPC title

• H01M50/491

  Porosity · CPC title

• H01M50/489

  Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties · CPC title

• H01G11/52 Primary

  Separators · CPC title