Lithium ion capacitor

Patent metadata

Field	Value
Publication number	US-10002718-B2
Application number	US-201415037100-A
Country	US
Kind code	B2
Filing date	Nov 28, 2014
Priority date	Nov 29, 2013
Publication date	Jun 19, 2018
Grant date	Jun 19, 2018

Abstract

This lithium ion capacitor results from housing an electrode laminate body, which comprises a positive electrode, a negative electrode, and a separator, and a non-aqueous electrolyte, which contains a lithium-ion-containing electrolyte, in an external body, wherein the negative electrode has a negative electrode current collector and a negative electrode active material layer containing a negative electrode active material that can occlude and release lithium ions on one or both surfaces of the negative electrode current collector, and the following (i) to (iii) are all satisfied: (i) the negative electrode active material is a carbon composite material containing carbon black and a carbonaceous material; (ii) the negative electrode is doped with lithium ion at between 1,050 mAh/g and 2,500 mAh/g, inclusive, per unit mass of the negative electrode active material; and (iii) the thickness of the negative electrode active material layer is between 10 μm and 60 μm, inclusive, per side.

First claim

What is claimed is:

1. A lithium ion capacitor comprising:
an electrode laminate body comprising a positive electrode, a negative electrode and a separator;
a non-aqueous electrolyte solution including a lithium ion-containing electrolyte; and
an external body,
wherein the electrode laminate body and the non-aqueous electrolyte solution are housed in the external body,
wherein the negative electrode comprises:
a negative electrode current collector; and
a negative electrode active material layer that includes a negative electrode active material that occlude and release lithium ions, on one or both sides of the negative electrode current collector,

the negative electrode active material is a composite carbon material having a mean particle size (D50) between 5 μm and 20 μm, inclusive, and comprising carbon black and a carbonaceous material,
(ii) the negative electrode is doped with lithium ion at between 1,050 mAh/g and 2,500 mAh/g, inclusive, per unit mass of the negative electrode active material, and
(iii) the thickness of the negative electrode active material layer is between 10 μm and 60 μm, inclusive, per side.

2. The lithium ion capacitor according to claim 1 , wherein the thickness of the negative electrode active material layer is between 10 μm and 40 μm, inclusive, per side.

3. The lithium ion capacitor according to claim 1 , wherein the electrode peel strength of the negative electrode is 0.20 N/cm or greater.

4. The lithium ion capacitor according to claim 1 , wherein the specific surface area of the composite carbon material as calculated by the BET method is between 100 m 2 /g and 350 m 2 /g, inclusive.

5. The lithium ion capacitor according to claim 1 ,
wherein the negative electrode has an initial charge capacity of between 700 mAh/g and 1,600 mAh/g, inclusive, per unit mass of the negative electrode active material, when lithium metal is used as the counter electrode to form a lithium ion capacitor, and when constant-current charge has been conducted with a current value of 0.5 mA/cm 2 to a voltage value of 0.01 V, and then constant voltage charge is conducted until the current value reaches 0.01 mA/cm 2 , at a measuring temperature of 25° C.

6. The lithium ion capacitor according to claim 1 , wherein the composite carbon material is produced by baking or graphitizing a kneaded mixture of 100 parts by mass of carbon black and between 30 parts by mass and 200 parts by mass, inclusive of a precursor of the carbonaceous material.

7. The lithium ion capacitor according to claim 1 , wherein the composite carbon material is produced by:
baking or graphitizing a kneaded mixture at 800° C. to 3,200° C., wherein the kneaded mixture is obtained by kneading:
the carbon black having a mean particle size of 12 to 300 nm as observed under an electron microscope, and a specific surface area of 200 to 1,500 m 2 /g as determined by the BET method, and
a precursor of the carbonaceous material; and

pulverizing baked or graphitized the mixture to a mean particle size (D50) of 1 to 20 μm.

8. The lithium ion capacitor according to claim 1 , wherein the positive electrode has:
a positive electrode current collector; and a positive electrode active material layer including a positive electrode active material on one or both sides of the positive electrode current collector, and
wherein the positive electrode active material is active carbon satisfying the inequalities 0.3<V1≤0.8 and 0.5≤V2≤1.0, where V1 (cc/g) is the mesopore volume due to pores with diameters of between 20 angstrom and 500 angstrom, inclusive, as calculated by the BJH method, and V2 (cc/g) is the micropore volume due to pores with diameters of smaller than 20 angstrom as calculated by the MP method, and having a specific surface area of between 1,500 m 2 /g and 3,000 m 2 /g, inclusive, as measured by the BET method.

9. The lithium ion capacitor according to claim 1 , wherein the positive electrode has:
a positive electrode current collector; and a positive electrode active material layer including a positive electrode active material on one or both sides of the positive electrode current collector, and
wherein the positive electrode active material is active carbon satisfying the inequalities 0.8<V1≤2.5 and 0.8<V2≤3.0, where V1 (cc/g) is the mesopore volume due to pores with diameters of between 20 angstrom and 500 angstrom, inclusive, as calculated by the BJH method, and V2 (cc/g) is the micropore volume due to pores with diameters of smaller than 20 angstrom as calculated by the MP method, and having a specific surface area of between 3,000 m 2 /g and 4,000 m 2 /g, inclusive, as measured by the BET method.

10. The lithium ion capacitor according to claim 2 , wherein the electrode peel strength of the negative electrode is 0.20 N/cm or greater.

11. The lithium ion capacitor according to claim 2 , wherein the specific surface area of the composite carbon material as calculated by the BET method is between 100 m 2 /g and 350 m 2 /g, inclusive.

12. The lithium ion capacitor according to claim 6 , wherein the specific surface area of the composite carbon material as calculated by the BET method is between 100 m2/g and 350 m2/g, inclusive.

13. The lithium ion capacitor according to claim 2 ,
wherein the negative electrode has an initial charge capacity of between 700 mAh/g and 1,600 mAh/g, inclusive, per unit mass of the negative electrode active material, when lithium metal is used as the counter electrode to form a lithium ion capacitor, and when constant-current charge has been conducted with a current value of 0.5 mA/cm 2 to a voltage value of 0.01 V, and then constant voltage charge is conducted until the current value reaches 0.01 mA/cm 2 , at a measuring temperature of 25° C.

14. The lithium ion capacitor according to claim 3 ,
wherein the negative electrode has an initial charge capacity of between 700 mAh/g and 1,600 mAh/g, inclusive, per unit mass of the negative electrode active material, when lithium metal is used as the counter electrode to form a lithium ion capacitor, and when constant-current charge has been conducted with a current value of 0.5 mA/cm 2 to a voltage value of 0.01 V, and then constant voltage charge is conducted until the current value reaches 0.01 mA/cm 2 , at a measuring temperature of 25° C.

15. The lithium ion capacitor according to claim 6 , wherein the negative electrode has an initial charge capacity of between 700 mAh/g and 1,600 mAh/g, inclusive, per unit mass of the negative electrode active material, when lithium metal is used as the counter electrode to form a lithium ion capacitor, and when constant-current charge has been conducted with a current value of 0.5 mA/cm2 to a voltage value of 0.01 V, and then constant voltage charge is conducted until the current value reaches 0.01 mA/cm2, at a measuring temperature of 25° C.

16. The lithium ion capacitor according to claim 4 ,
wherein the negative electrode has an initial charge capacity of between 700 mAh/g and 1,600 mAh/g, inclusive, per unit mass of the negative electrode active material, when lithium metal is used as the counter electrode to form a lithium ion capacitor, and when constant-current charge has been conducted with a current value of 0.5 mA/cm 2 to a voltage value of 0.01 V, and then constant voltage charge is conducted until the current value reaches 0.01 mA/cm 2 , at a measuring temperature of 25° C.

Assignees

• Asahi Chemical Ind

Inventors

• Kamijo Takeshi
• Okada Nobuhiro
• Kimura Yuima

Classifications

• Y02E60/13

  Energy storage using capacitors · CPC title

• H01G11/42

  Powders or particles, e.g. composition thereof · CPC title

• H01G11/66

  Current collectors · CPC title

• H01G11/62

  characterised by the solute, e.g. salts, anions or cations therein · CPC title

• H01G11/24

  characterised by structural features of the materials making up or comprised in the electrodes, e.g. form, surface area or porosity; characterised by the structural features of powders or particles used therefor · CPC title