Low-cost fine-grain weak-texture magnesium alloy sheet and method of manufacturing the same

Patent metadata

Field	Value
Publication number	US-10000836-B2
Application number	US-201414773996-A
Country	US
Kind code	B2
Filing date	Mar 13, 2014
Priority date	May 7, 2013
Publication date	Jun 19, 2018
Grant date	Jun 19, 2018

Abstract

The present invention discloses a Mg—Ca—Zn—Zr magnesium alloy sheet, having the chemical compositions in weight percentage: Ca: 0.5˜1.0%, Zn: 0.4˜1.0%, Zr: 0.5˜1.0%, the remainders being Mg and unavoidable impurities; wherein the magnesium alloy sheet has an average grain size of less than or equal to 10 μm, an interarea texture strength of less than or equal to 5, an interarea texture strength after annealing at 250˜400° C. of less than or equal to 3, and a limiting drawing ratio at room temperature of more than AZ31; and the grain size thereof is remarkably less than that of AZ31B sheet produced in the same conditions, and the sheet texture is notably weakened. The magnesium alloy of the present invention has simple chemical compositions without noble alloy elements therein, thereby having a wide applicability and a low manufacturing cost, which can act as the sheets of interior door panels of cars, inner panels of engine lids, inner panels of trunk lids, internal decorative panels, vehicle bodies in the rail transits, and housings of 3C products, or the like.

First claim

What is claimed is:

1. A Mg—Ca—Zn—Zr magnesium alloy sheet, having the chemical compositions in weight percentage: Ca: 0.5˜1.0%, Zn: 0.4˜1.0%, Zr: 0.5˜1.0%, the remainders being Mg and unavoidable impurities; wherein the magnesium alloy sheet has an average grain size of less than or equal to 10 μm, an interarea texture strength of less than or equal to 5, an interarea texture strength after annealing at 250˜400° C. of less than or equal to 3, and a limiting drawing ratio at room temperature of more than 1.74; and the magnesium alloy sheet has a thickness of 0.3˜4 mm.

2. A method of producing the Mg—Ca—Zn—Zr magnesium alloy sheet according to claim 1 , which is any one of the following methods (1)˜(3):
(1) heating the casting blank of Mg—Ca—Zn—Zr magnesium alloy with the aforementioned composition proportions up to a temperature of 370˜500° C., and carrying out solid solution, then hot rolling and warm rolling, so as to obtain the Mg—Ca—Zn—Zr magnesium alloy sheet with a thickness of 0.3˜4 mm; wherein the heat preservation time in the solid solution is 0.5˜1 min/mm;
when in the hot rolling, the roller surfaces are preheated at 150˜350° C., the blooming temperature is 450˜500° C., the finish rolling temperature is 300˜350° C., and the reduction rate in a single pass is 20˜50%;
when in the warm rolling, the roller surfaces are preheated up to 150˜350° C., the magnesium alloy sheet is online concurrent heated, the rolling temperature is 150˜350° C., and the reduction rate in a single pass is 20˜40%;
(2) pouring the magnesium alloy melt with the aforementioned composition proportions into a twin-roller continuous cast-rolling mill for cast-rolling, so as to obtain the cast-rolling coil; carrying out solid solution and warm rolling, or warm rolling directly, so as to obtain the Mg—Ca—Zn—Zr magnesium alloy sheet with a thickness of 0.3˜4 mm;
wherein in the cast-rolling process by the twin-roller continuous cast-rolling mill, the rotation linear velocity of the rollers is 5-10 m/min, the roller gap is 4-8 mm, the roller surfaces are lubricated by graphite, and the gases N 2 and CO 2 pass through the smelter and casting system and SO 2 passes through the pouring exit for protection;
the temperature of the solid solution is 370˜500° C., and the heat preservation time thereof is 0.5˜1 min/mm;
when in the warm rolling, the roller surfaces are preheated up to 180˜300° C., the magnesium alloy sheet is online concurrent heated, the rolling temperature is 180˜300° C., and the reduction rate in a single pass is 20˜40%;
(3) heating the casting blank of magnesium alloy with the aforementioned composition proportions up to a temperature of 370˜500° C., and carrying out solid solution, then performing horizontal extrusion, so as to obtain the Mg—Ca—Zn—Zr magnesium alloy sheet with a thickness of 2˜4 mm, or performing horizontal extrusion and subsequently warm rolling, so as to obtain the Mg—Ca—Zn—Zr magnesium alloy sheet with a thickness of 0.3˜2 mm;
wherein the heat preservation time in the solid solution is 0.5˜1 min/mm;
when in the horizontal extrusion, the extrusion container and die are preheated up to 400˜500° C., the extrusion temperature is 350˜500° C., and the extrusion rate is 2˜10 m/min; and
when in the warm rolling, the roller surfaces are preheated up to 150˜300° C., the magnesium alloy sheet is online concurrent heated, the rolling temperature is 150˜300° C., and the reduction rate in a single pass is 30˜50%.

3. The method of producing Mg—Ca—Zn—Zr magnesium alloy sheet according to claim 2 , wherein it further comprises a cold rolling stage, wherein the cold rolling reduction rate is 10˜20%, and the thickness of the finished sheet is about 0.3 mm.

4. The method of producing Mg—Ca—Zn—Zr magnesium alloy sheet according to claim 2 , wherein it further comprises an annealing treatment and/or an aging treatment; wherein the annealing temperature is 250˜400° C., and the aging temperature is 150˜200° C.

5. The method of producing Mg—Ca—Zn—Zr magnesium alloy sheet according to claim 3 , wherein it further comprises an annealing treatment and/or an aging treatment; wherein the annealing temperature is 250˜400° C., and the aging temperature is 150˜200° C.

Assignees

• Baoshan Iron & Steel

Inventors

• Liang Gaofei
• Zhang Yongjie
• Yang Qi
• Wang Gang

Classifications

• C22C23/04

  with zinc or cadmium as the next major constituent · CPC title

• C22C23/00

  Alloys based on magnesium · CPC title

• C22F1/06 Primary

  of magnesium or alloys based thereon · CPC title

• B22D21/007

  with low melting point, e.g. Al 659 degrees C, Mg 650 degrees C · CPC title

• B22D23/00

  Casting processes not provided for in groups B22D1/00 - B22D21/00 (making metallic powder by casting B22F9/08; alumino-thermic welding B23K23/00; remelting metals C22B9/16) · CPC title